Room-temperature Schottky diodes and the onset of the ferroelectricity in ZrO2/Si heterostructures
Source abstract
Abstract
Abstract In this paper we investigate three different heterostructures, all based on ZrO 2 grown by ALD (atomic layer deposition), and having each thickness in the range 7–20 nm. These are: metal -insulator-semiconductor (MIS) Au/ZrO 2 /doped Si, and metal -insulator-metal (MIM) Au/ZrO 2 /Pt/doped Si, Pt/ZrO 2 /Pt/doped Si. We have measured their current-voltage characteristics at room temperature and their associate ferroelectricity before and after a rapid thermal annealing (RTA) treatment. High performances nanoscale Schottky diodes were obtained after RTA at the ZrO 2 thickness of 15 nm. In the case of the MIS diodes the ideality factor was 1.56 and |2P r | = 20.6 µC/cm 2 , while in the case of the MIM diodes the best diodes were Pt/ZrO 2 /Pt/ with an ideality factor of 2.03 and |2P r | = 47.9 µC/cm 2 and a leakage current in the range 10–50 fA. The subthreshold swing of 31.6 mV/decade and an on/off ratio of 10 7 show that these ZrO 2 -based MIM diodes are an excellent candidate for low-power logic applications.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Ferroelectric and Negative Capacitance Devices · Semiconductor materials and devices · Semiconductor materials and interfaces
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (29)
Show source-provided references
1. W. Cao, H. Bu, M. Vinet, M. Cao, S. Takagi, S. Hwang, T. Ghani, K. Banerjee, The future transistors. Nature. 620, 501–515 (2023)10.1038/s41586-023-06145-x ↗
2. T.S. Böscke, J. Müller, D. Bräuhaus, U. Schröder, U. Böttger, Ferroelectricity in hafnium oxide thin films. Appl. Phys. Lett. 99, 102903 (2011)10.1063/1.3634052 ↗
3. D. Lehninger, F. Müller, Y. Raffel, S. Yang, M. Neuber, S. Abdulazhanov, T. Kämpfe, K. Seidel, M. Lederer, Ferroelectric hafnium oxide: a potential game-changer for nanoelectronic devices and systems. Adv. Electron. Mater. 11, 2400686 (2025)10.1002/aelm.202400686 ↗
4. M. Dragoman, M. Aldrigo, D. Dragoman, S. Iordanescu, A. Dinescu, M. Modreanu, HfO2-based ferroelectrics applications in nanoelectronics. physica status solidi (RRL) – Rapid Research Letters 15, 2000521 (2021)10.1002/pssr.202000521 ↗
5. J. Müller, T.S. Böscke, U. Schröder, S. Mueller, D. Bräuhaus, U. Böttger, L. Frey, T. Mikolajick, Ferroelectricity in simple binary ZrO2 and HfO2. Nano Lett. 12, 4318–4323 (2012)10.1021/nl302049k ↗
6. Y. Si, T. Zhang, C. Liu, S. Das, B. Xu, R.G. Burkovsky, X.-K. Wei, Z. Chen, Antiferroelectric oxide thin-films: fundamentals, properties, and applications. Prog. Mater. Sci. 142, 101231 (2024)10.1016/j.pmatsci.2023.101231 ↗
7. W. Yang, C. Yu, H. Li, M. Fan, X. Song, H. Ma, Z. Zhou, P. Chang, P. Huang, F. Liu, Ferroelectricity of hafnium oxide-based materials: current status and future prospects from physical mechanisms to device applications. J. Semicond. 44, 053101 (2023)10.1088/1674-4926/44/5/053101 ↗
8. K. Xu, T. Wang, J. Yu, Y. Liu, Z. Li, C. Lu, J. Song, J. Meng, H. Zhu, Q. Sun, D.W. Zhang, L. Chen, Fluorite-structured antiferroelectric hafnium-zirconium oxide for emerging nonvolatile memory and neuromorphic computing applications. Appl. Phys. Rev. 11, 021303 (2024)10.1063/5.0175439 ↗
9. J.P.B. Silva, R. Alcala, U.E. Avci, N. Barrett, L. Bégon-Lours, M. Borg, S. Byun, S.-C. Chang, S.-W. Cheong, D.-H. Choe, J. Coignus, V. Deshpande, A. Dimoulas, C. Dubourdieu, I. Fina, H. Funakubo, L. Grenouillet, A. Gruverman, J. Heo, M. Hoffmann, H.A. Hsain, F.-T. Huang, C.S. Hwang, J. Íñiguez, J.L. Jones, I.V. Karpov, A. Kersch, T. Kwon, S. Lancaster, M. Lederer, Y. Lee, P.D. Lomenzo, L.W. Martin, S. Martin, S. Migita, T. Mikolajick, B. Noheda, M.H. Park, K.M. Rabe, S. Salahuddin, F. Sánchez, K. Seidel, T. Shimizu, T. Shiraishi, S. Slesazeck, A. Toriumi, H. Uchida, B. Vilquin, X. Xu, K.H. Ye, U. Schroeder, Roadmap on ferroelectric hafnia- and zirconia-based materials and devices. APL Mater. 11, 089201 (2023)10.1063/5.0148068 ↗
10. D.-C. Hsu, M.-T. Wang, J.Y. Lee, P.-C. Juan, Electrical characteristics and reliability properties of metaloxide-semiconductor field-effect transistors with gate dielectric. J. Appl. Phys. 101, 094105 (2007)10.1063/1.2723861 ↗
11. https://rmis.jrc.ec.europa.eu/rmp/Hafnium
12. S.S. Cheema, N. Shanker, S.-L. Hsu, Y. Rho, C.-H. Hsu, V.A. Stoica, Z. Zhang, J.W. Freeland, P. Shafer, C.P. Grigoropoulos, J. Ciston, S. Salahuddin, Emergent ferroelectricity in subnanometer binary oxide films on silicon. Science 376, 648–652 (2022)10.1126/science.abm8642 ↗
13. J. Wang, D. Zhou, W. Dong, X. Hou, F. Liu, N. Sun, F. Ali, Z. Li, Ferroelectric properties of pure ZrO2 thin films by chemical solution deposition. Ceram. Int. 47, 16845–16851 (2021)10.1016/j.ceramint.2021.02.259 ↗
14. Y.-S. Jiang, K.-W. Huang, S.-H. Yi, C.-I. Wang, T.-J. Chang, W.-C. Kao, C.-Y. Wang, Y.-T. Yin, J. Shieh, M.-J. Chen, Ferroelectric ZrO2 ultrathin films on silicon for metal-ferroelectric-semiconductor capacitors and transistors. J. Eur. Ceram. Soc. 42, 6997–7003 (2022)10.1016/j.jeurceramsoc.2022.07.031 ↗
15. X. Li, Z. Xu, S. Hu, M. Gu, Y. Zhu, Q. Liu, Y. Yang, M. Ye, J. Li, L. Chen, Ferroelectricity in orthorhombic zirconia thin films. Nano Lett 25, 4220–4226 (2025)10.1021/acs.nanolett.4c05612 ↗
16. Z. Wang, Z. Guan, H. Wang, X. Zhou, J. Li, S. Shen, Y. Yin, X. Li, Pure ZrO2 ferroelectric thin film for nonvolatile memory and neural network computing. ACS Appl. Mater. Interfaces 16, 22122–22130 (2024)10.1021/acsami.4c01234 ↗
17. F.-C. Chiu, Z.-H. Lin, C.-W. Chang, C.-C. Wang, K.-F. Chuang, C.-Y. Huang, J.Y. Lee, H.-L. Hwang, Electron conduction mechanism and band diagram of sputter-deposited Al/ ZrO 2 / Si structure. J. Appl. Phys. 97, 034506 (2005)10.1063/1.1846131 ↗
18. M.G. Obaid, Y.S. Ocak, B.A. Albiss, M. Benhaliliba, Electrical and photoelectrical characterization of Au/ n‑Si diode with sputtered ZrO2 interlayer. J. Mater. Sci. Mater. Electron. 34, 1768 (2023).10.1007/s10854-023-11160-9 ↗
19. S.-H. Yi, B.-T. Lin, T.-Y. Hsu, J. Shieh, M.-J. Chen, Modulation of ferroelectricity and antiferroelectricity of nanoscale ZrO2 thin films using ultrathin interfacial layers. J. Eur. Ceram. Soc. 39, 4038–4045 (2019)10.1016/j.jeurceramsoc.2019.05.065 ↗
20. M.-T. Wang, T.-H. Wang, J.Y. Lee, Electrical conduction mechanism in high-dielectric-constant ZrO2 thin films. Microelectron. Reliab. 45, 969–972 (2005)10.1016/j.microrel.2004.11.014 ↗
21. H. Dan, L. Chen, Z. Li, X. He, Y. Ding, Preparation of amorphous ZrO2 powders by hydrothermal-assisted sol-gel method. Inorg. Chem. Commun. 138, 109272 (2022)10.1016/j.inoche.2022.109272 ↗
22. B.T. Lin, Y.-W. Lu, J. Shieh, M.-J. Chen, Induction of ferroelectricity in nanoscale ZrO2 thin films on Pt electrodes without post-annealing. J. European Ceramic Society 37, 1135–1139 (2012)10.1016/j.jeurceramsoc.2016.10.028 ↗
23. X. Lyu, J. Zou, F. Ali, I. Fina, F. Sánchez, Intrinsic ferroelectric polarization in doped HfO2 and ZrO2. Small 21, e6334 (2025)10.1002/smll.202506334 ↗
24. K.W. Huang, S.-H. Yi, Y.-S. Jiang, W.-C. Kao, Y-Tung. Yin, D. Beck, V. Korolkov, R. Proksch, Jay Shieh, M.-J. Chen, Sub-7-nm textured ZrO 2 with giant ferroelectricity. Acta Mater. 205, 116536 (2021)10.1016/j.actamat.2020.116536 ↗
25. C. Ge, C. Wang, K.-J. Jin, H.-B. Lu, G.-Z. Yang, Recent progress in ferroelectric diodes: explorations in switchable diode effect. Nano-Micro Lett. 5(2), 81–87 (2013)10.1007/BF03353733 ↗
26. J. Yao, Y. Liu, S. Ding, Y. Zhu, Z. Mao, S.V. Kalinin, Y. Liu, Ferroelectric schottky diodes of CuInP2S6 nanosheet. Appl. Phys. Lett. 123, 142903 (2023)10.1063/5.0160928 ↗
27. P.W.M. Blom, R.M. Wolf, J.F.M. Cillessen, M.P.C.M. Krijn, Ferroelectric schottky diode. Phys. Rev.Lett 73, 2107–2110 (1994)10.1103/PhysRevLett.73.2107 ↗
28. B. Wang, W. Chen, L. Zou, T. Wang, Z. Li, Z. Wang, H. Xu, L. Xu, S. Lan, P. Feng, Y. Ma, D. Zheng, Xin He, Yang Xu, Z. Luo, Z. Wu, Y. Liu, G. Han, Xi.. Zhang, B. Yu, F. Xue, A programmable nonvolatile Schottky diode based on van der Waals ferroelectric junction. Nano Lett. 25, 10699–10708 (2025)10.1021/acs.nanolett.5c02646 ↗
29. Z. Xi, J. Ruan, C. Li, C. Zheng, Z. Wen, J. Dai, A. Li, D. Wu, Giant tunnelling electroresistance in metal/ferroelectric/semiconductor tunnel junctions by engineering the Schottky barrier. Nat. Commun. 8, 15217 (2017)10.1038/ncomms15217 ↗