Structural and property changes in poly (vinylidene fluoride–trifluoroethylene) 70/30 mol % copolymer induced by proton irradiation

Poly(vinylidene fluoride–trifluoroethylene) 70/30 mol % copolymer has been irradiated with 3 MeV protons at doses ranging from 43 to 200 Mrad. The effects of irradiation on the polarization hysteresis, dielectric properties, lattice spacing, phase transition behavior and electric-field-induced strain have been studied. The irradiated copolymer exhibits the characteristic behavior of a relaxor ferroelectric, including frequency dispersion of the dielectric constant, which follows the Vogel–Fulcher rule. These results indicate that the proton irradiation breaks up the coherent polarization domains in the copolymer into nano-sized regions, thereby converting the copolymer to a relaxor ferroelectric. X-ray diffraction measurements show that the nano-sized regions are in the non-polar phase. Since the lattice spacing of the non-polar phase is substantially different from that of the polar phase, the local phase transformation between these two phases induced by an external electric field gives rise to a large lattice strain and hence a giant electrostrictive response.