Improved switching performance of magnetic tunnel junctions with Heusler compounds by insertion of resistive layers
Source abstract
Abstract
The chemical templating layer (CTL) is ideally suited to grow ordered multicomponent Heusler compounds at temperatures compatible with complementary metal–oxide–semiconductor technology and at thickness necessary for their implementation as storage layers in magnetic random-access memory (MRAM). In current MRAM technology, the storage layer is either capped or seeded with oxide layers (i.e., sandwiched between two resistive layers), primarily to suppress effective Gilbert damping. The CTL, which is metallic and in contact with the storage layer, is expected to enhance the effective damping constant of the Heusler compound due to spin-pumping effect leading to a high switching current. We demonstrate two approaches to mitigate this by inserting ultrathin resistive layers of either MgO or ScN in proximity to the CTL/Heusler interface. The ∼4 Å-thick MgO layer is discontinuous, containing voids filled with CTL that transfers templating information from the underlying thick CTL layer to the Heusler compound. The ScN layer is thick (∼50 Å) and promotes ordering in the Heusler compound via an ultrathin CTL layer (∼20 Å). The magnetic tunnel junction devices with such resistive layers have higher efficiency and operate at lower switching currents.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Magnetic properties of thin films · Heusler alloys: electronic and magnetic properties · ZnO doping and properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
IBM Research – Almaden 1 , San Jose, California 95120,
Samsung Semiconductor Inc. 2 , San Jose, California 95134,
Max Plank Institute for Microstructure Physics 3 , Weinberg 2, 06120 Halle (Saale),
References (20)
Show source-provided references
1. Origin of the tetragonal ground state of Heusler compounds10.1103/PhysRevApplied.7.034022 ↗
2. Neutron diffraction study of Mn3Ge
3. Ferrimagnetic Heusler tunnel junctions with fast spin-transfer torque switching enabled by low magnetization10.1038/s41565-024-01827-7 ↗
4. Nanometer-thin L1-MnAl film with B2-CoAl underlayer for high-speed and high-density STT-MRAM: Structure and magnetic properties10.1063/5.0077874 ↗
5. Giant tunnelling magnetoresistance at room temperature with MgO (100) tunnel barriers10.1038/nmat1256 ↗
6. Giant room-temperature magnetoresistance in single-crystal Fe/MgO/Fe magnetic tunnel junctions10.1038/nmat1257 ↗
7. Termination layer compensated tunnelling magnetoresistance in ferrimagnetic Heusler compounds with high perpendicular magnetic anisotropy10.1038/ncomms10276 ↗
8. Heusler compounds with perpendicular magnetic anisotropy and large tunneling magnetoresistance10.1103/PhysRevMaterials.1.024402 ↗
9. Tunnel barrier enhanced voltage signal generated by magnetization precession of a single ferromagnetic layer10.1103/PhysRevLett.100.067602 ↗
10. Suppression of spin-pumping by a MgO tunnel-barrier10.1063/1.3280378 ↗
11. Ferromagnetic resonance and damping properties of CoFeB thin films as free layers in MgO-based magnetic tunnel junctions10.1063/1.3615961 ↗
12. Spin transfer switching in dual MgO magnetic tunnel junctions10.1063/1.2717556 ↗
13. Enhanced Gilbert damping in thin ferromagnetic films10.1103/PhysRevLett.88.117601 ↗
14. Development of semiconducting ScN10.1103/PhysRevMaterials.3.020301 ↗
15. Enhancement in tunnel magnetoresistance for magnetic tunnel junctions in Mn based Heusler compounds10.1063/5.0271566 ↗
16. Chiral domain wall motion in unit-cell thick perpendicularly magnetized Heusler films prepared by chemical templating10.1038/s41467-018-07091-3 ↗
17. Thermally assisted magnetization reversal in the presence of a spin-transfer torque10.1103/PhysRevB.69.134416 ↗
18. Currents, torques, and polarization factors in magnetic tunnel junctions10.1103/PhysRevB.71.024411 ↗
19. Spin-transfer torque switched magnetic tunnel junctions in magnetic random access memory10.1117/12.2238712 ↗
20. Spin-transfer pulse switching: From the dynamic to the thermally activated regime10.1063/1.3532960 ↗