Origins of infrared transparency in highly conductive perovskite stannate BaSnO3

Y. Smirnov, J. Holovsky, G. Rijnders, M. Morales-Masis

APL Materials· Volume 8· Issue 6

Abstract

Near-infrared absorption in transparent conducting oxides (TCOs) is usually caused by electronic intraband transition at high doping levels. Improved infrared transparency is commonly explained by enhanced drift mobility in these TCOs. Here, an alternative cause behind the high infrared transparency of La-doped barium stannate (LBSO) transparent electrodes is presented. Following the Drude model formalism, we reconstructed spectrally resolved dielectric permittivity for a set of thin films with different free electron concentrations. A comparison of optical properties of LBSO with the tin-doped indium oxide thin films with identical carrier concentrations suggests that the redshift of the screened plasma wavelength for LBSO originates from its large high-frequency dielectric constant of 4.4, one of the highest reported for the s-orbital-based TCOs. Moreover, our measurements confirm an optical mobility significantly higher (>300 cm2/V s) than the drift mobility, effectively suppressing the free carrier absorption. These factors enable high infrared transparency of LBSO films and motivate further exploration of LBSO as broadband TCOs for solar cells and nanophotonics.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Electronic and Structural Properties of Oxides · ZnO doping and properties · Magnetic and transport properties of perovskites and related materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

MESA+ Institute for Nanotechnology, University of Twente 1 , Enschede, 7500 AE, The Netherlands

Institute of Physics, Czech Academy of Sciences 2 , v. v. i., Cukrov1arnická 10, 162 00 Prague, Czech Republic

Faculty of Electrical Engineering, Czech Technical University in Prague 3 , Technická 2, 166 27 Prague, Czech Republic

Funding

SOLAR-ERA.NET, CUSTCO Project · Grantová Agentura České Republiky · University of Twente

References (36)

Show source-provided references
1. Adv. Electron. Mater. · 2017 · 3 · 160052910.1002/aelm.201600529 ↗
2. J. Opt. Soc. Am. B · 2015 · 32 · 12110.1364/josab.32.000121 ↗
3. 2013
4. Thin Solid Films · 1983 · 102 · 110.1016/0040-6090(83)90256-0 ↗
5. 2010
6. J. Appl. Phys. · 2006 · 100 · 05490510.1063/1.2222070 ↗
7. Appl. Phys. Express · 2008 · 1 · 04150110.1143/apex.1.041501 ↗
8. Chem. Mater. · 2015 · 27 · 278810.1021/cm503896h ↗
9. Phys. Rev. Mater. · 2019 · 3 · 08460810.1103/physrevmaterials.3.084608 ↗
10. 2002
11. Appl. Phys. Express · 2012 · 5 · 06110210.1143/apex.5.061102 ↗
12. APL Mater. · 2014 · 2 · 05610710.1063/1.4874895 ↗
13. APL Mater. · 2017 · 5 · 11610710.1063/1.5001839 ↗
14. APL Mater. · 2019 · 7 · 02250710.1063/1.5054154 ↗
15. APL Mater. · 2015 · 3 · 03610110.1063/1.4913587 ↗
16. APL Mater. · 2020 · 8 · 01111010.1063/1.5133745 ↗
17. Superlattices Microstruct. · 2016 · 96 · 20510.1016/j.spmi.2016.05.027 ↗
18. Appl. Phys. Lett. · 2016 · 108 · 17210110.1063/1.4948355 ↗
19. Appl. Phys. Lett. · 1980 · 36 · 13010.1063/1.91395 ↗
20. Thin Solid Films · 2016 · 618 · 13010.1016/j.tsf.2016.04.026 ↗
21. Opt. Commun. · 1986 · 57 · 33610.1016/0030-4018(86)90270-1 ↗
22. Appl. Surf. Sci. · 2001 · 175-176 · 54310.1016/s0169-4332(01)00145-3 ↗
23. J. Appl. Phys. · 2013 · 113 · 01310710.1063/1.4772975 ↗
24. Low-temperature high-mobility amorphous IZO for silicon heterojunction solar cells10.1109/jphotov.2015.2450993 ↗
25. Phys. Rev. B · 2012 · 86 · 16520510.1103/physrevb.86.165205 ↗
26. Phys. Rev. B · 2017 · 95 · 16120210.1103/physrevb.95.161202 ↗
27. J. Appl. Phys. · 2012 · 112 · 04410810.1063/1.4748309 ↗
28. J. Appl. Phys. · 2007 · 101 · 03312510.1063/1.2434005 ↗
29. J. Appl. Phys. · 2014 · 116 · 04370510.1063/1.4891225 ↗
30. Far infrared dielectric dispersion in BaTiO3, SrTiO3, and TiO210.1103/physrev.126.1710 ↗
31. Physica B · 2007 · 393 · 23910.1016/j.physb.2007.01.008 ↗
32. J. Appl. Phys. · 1986 · 60 · R12310.1063/1.337534 ↗
33. Phys. Rev. B · 2005 · 71 · 07510910.1103/physrevb.71.075109 ↗
34. J. Appl. Phys. · 1980 · 51 · 624310.1063/1.327610 ↗
35. J. Appl. Phys. · 1989 · 65 · 127010.1063/1.343022 ↗
36. Phys. Rev. B · 2020 · 101 · 12520610.1103/physrevb.101.125206 ↗