Direct neutron-diffraction-based measurement of magnetic order in brownmillerite SrCoO2.5 and La0.5Sr0.5CoO2.5 thin films

Epitaxial cobaltites have emerged as exemplary materials for electrochemical gating, in large part due to their topotactic perovskite (P) ↔ brownmillerite (BM) transformations. SrCoO3−δ, for example, can be cycled between metallic ferromagnetic P SrCoO3 and insulating BM SrCoO2.5, realizing exceptional modulation of electronic, thermal, and optical properties. It is often presumed that such cycling also generates ferromagnetic–antiferromagnetic (F-AF) modulation due to the G-type AF order in bulk SrCoO2.5. Little is understood about magnetism in thin-film BM SrCoO2.5, however, meaning that the true magnetic property modulation is unclear. We address this here through a neutron diffraction study of BM La1−xSrxCoO2.5 films at x = 0.5 and 1.0. Lightly compressively strained SrCoO2.5 films are shown to retain G-type AF order, albeit with suppressed Néel temperature (∼340 K). Of high interest for AF spintronics, room-temperature F–AF cycling is thus possible across the SrCoO3-δ P ↔ BM transformation. At x = 0.5, however, BM La0.5Sr0.5CoO2.5 films are found to exhibit no detectable G-type AF order but instead weak F order (Curie temperature ∼115 K), unveiling a La0.5Sr0.5CoO3−δ phase diagram with two distinct F phases. These results thus uncover new, unanticipated magnetic phase behavior in these materials, in addition to being directly relevant to cobaltite-based magnetoionics.