Large enhancement of the electrocaloric effect in PLZT ceramics prepared by hot-pressing
Source abstract
Abstract
In this contribution, we demonstrate the optimization of the microstructures of the Pb0.85La0.1(Zr0.65Ti0.35)O3 (PLZT) relaxor ferroelectric ceramics and subsequent enhancements in their polarization and electrical resistivity by using a hot-pressing process. The resulting superior breakdown strength of hot-pressed PLZT enables the application of high electric field to induce a giant electrocaloric effect, in which the adiabatic change of temperature (ΔT) and the isothermal change of entropy (ΔS) are around 2 times greater than those of the samples prepared by the conventional sintering approach using muffle furnace. Moreover, the addition of extra PbO to make up the loss of Pb in the high-temperature sintering leads to the further improvements in the phase composition and electrical properties of PLZT, due to inhibition of the pyrochlore phase formation. The relationship among the sintering conditions, the content of excess PbO, and the microstructure as well as the electrical characteristics of PLZT have been investigated in a systematic manner. This work provides a facile approach to enhanced electrocaloric effect in bulk ceramics.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Ferroelectric and Piezoelectric Materials · Dielectric materials and actuators · Microwave Dielectric Ceramics Synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
The Pennsylvania State University 1 Department of Materials Science and Engineering, , University Park, Pennsylvania 16802, USA
Huazhong University of Science and Technology 2 School of Optical and Electronic Information, , Wuhan, Hubei 430074, China
Huazhong University of Science and Technology 3 Wuhan National Laboratory for Optoelectronics, , Wuhan, Hubei 430074, China
Funding
National Science Foundation · National Natural Science Foundation of China
References (31)
Show source-provided references
1. Nat. Mater. · 2014 · 13 · 43910.1038/nmat3951 ↗
2. 2014
3. MRS Bull. · 2014 · 39 · 109910.1557/mrs.2014.256 ↗
4. Prog. Mater. Sci. · 2012 · 57 · 98010.1016/j.pmatsci.2012.02.001 ↗
5. Annu. Rev. Mater. Res. · 2011 · 41 · 22910.1146/annurev-matsci-062910-100341 ↗
6. Adv. Mater. · 2009 · 21 · 198310.1002/adma.200802902 ↗
7. Science · 2006 · 311 · 127010.1126/science.1123811 ↗
8. Science · 2008 · 321 · 82110.1126/science.1159655 ↗
9. Appl. Phys. Lett. · 2011 · 99 · 05290710.1063/1.3624533 ↗
10. Adv. Mater. · 2015 · 27 · 145010.1002/adma.201404591 ↗
11. Adv. Mater. · 2015 · 27 · 223610.1002/adma.201405495 ↗
12. ACS Nano · 2015 · 9 · 716410.1021/acsnano.5b03371 ↗
13. ACS Appl. Mater. Interfaces · 2014 · 6 · 1163310.1021/am502415z ↗
14. J. Am. Ceram. Soc. · 2015 · 98 · 117510.1111/jace.13412 ↗
15. J. Eur. Ceram. Soc. · 2012 · 32 · 89910.1016/j.jeurceramsoc.2011.10.054 ↗
16. J. Electroceram. · 2013 · 30 · 2410.1007/s10832-012-9701-z ↗
17. Ceram. Int. · 2013 · 39 · 370910.1016/j.ceramint.2012.10.204 ↗
18. J. Am. Ceram. Soc. · 2011 · 94 · 200310.1111/j.1551-2916.2011.04621.x ↗
19. J. Am. Ceram. Soc. · 1967 · 50 · 32910.1111/j.1151-2916.1967.tb15121.x ↗
20. Ceram. Int. · 2008 · 34 · 161710.1016/j.ceramint.2007.04.018 ↗
21. J. Eur. Ceram. Soc. · 2013 · 33 · 11310.1016/j.jeurceramsoc.2012.08.011 ↗
22. J. Am. Ceram. Soc. · 2013 · 96 · 102110.1111/jace.12219 ↗
23. Ceram. Int. · 2015 · 41 · S1510.1016/j.ceramint.2015.03.206 ↗
24. J. Appl. Phys. · 2011 · 110 · 06411810.1063/1.3641975 ↗
25. J. Appl. Phys. · 2011 · 109 · 12411110.1063/1.3596577 ↗
26. See supplementary material at http://dx.doi.org/10.1063/1.4950844 for SEM images and dielectric spectra of the samples.
27. Appl. Phys. Lett. · 2012 · 101 · 08290410.1063/1.4747275 ↗
28. J. Am. Ceram. Soc. · 1971 · 54 · 110.1111/j.1151-2916.1970.tb12105.x-i1 ↗
29. Phys. Rev. B · 2006 · 74 · 13411510.1103/PhysRevB.74.134115 ↗
30. J. Mech. Phys. Solids · 1993 · 41 · 115510.1016/0022-5096(93)90088-W ↗
31. J. Appl. Phys. · 1959 · 30 · 165010.1063/1.1735030 ↗