Influence of minor Ce additions on magnetic and electrical properties in Fe–6.5 wt. % Si alloy

Fe–6.5 wt. % Si alloys exhibit lower core loss at higher frequency than the dominating electrical steel containing 3.2% Si due to its lower magneto-crystalline anisotropy energy (MAE) and higher electrical resistivity. However, compared to nanocrystalline and amorphous soft-magnetic materials, 6.5% Si steel, although being cost effective and having high saturation magnetization, still has much to improve, especially with respect to MAE and resistivity. To explore further improvement, the effects of minor Ce additions (due to its mixed valence 4f-electron configuration) on the microstructure, electrical and magnetic behaviors of Fe–6.5 wt. % Si alloys were investigated. Due to its limited solubility in Fe, Ce exhibits condition-dependent effects on electrical resistivity, showing only marginal improvement under rapid solidification. In contrast, Ce addition degrades magnetic performance, reducing saturation magnetization (from 1.86 to 1.76 T) and increasing coercivity (from 88 to 171 A/m), which results in an 83.4% increase in core loss (W10/1000 condition). Overall, Ce addition provides limited benefit in electrical resistivity while deteriorating magnetic properties, making it ineffective for enhancing the soft magnetic performance of Fe–6.5 wt. % Si alloys.