Study on grooving corrosion behavior of QT800 coiled tubing
Source abstract
Abstract
The characteristics of grooving corrosion at a welding seam of QT800 coiled tubing were investigated under different conditions by using the conventional immersion test and constant potential accelerated corrosion test, respectively. The results showed that the sensitivity of grooving corrosion of the welded tube, represented by the grooving corrosion factor, was within the acceptable range even after the long-term immersion test. The reasons of the grooving corrosion were analyzed from the microstructure and electrochemical performance of the weld. Compared with the matrix and the heat-affected zone, the fusion line had coarse grains, large corrosion current, and low self-corrosion potential, which played a part in the main reason to induce the groove corrosion effect.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Welding Techniques and Residual Stresses · Surface Treatment and Residual Stress
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
College of Pipeline and Civil Engineering, China University of Petroleum 1 , Qingdao 266580, China
College of Petroleum Engineering, Xi’an Shiyou University 2 , Xi’an 710065, China
Puguang Branch of Zhongyuan Oilfield 3 , Puyang 457001, China
References (33)
Show source-provided references
1. Coiled tubing (CT) and its application technology development
2. Study on how to fish coiled tubing and application
3. Fracture failure analysis of Φ31.8 mm coiled tubing
4. Evaluation of corrosion resistance on domestic coiled velocity pipe string serviced for 3 years10.11973/fsyfh-201807004 ↗
5. Study on the coiled tubing erosion reliability
6. S. Shu-xian, “Research on axial fatigue property and M-A microstructure of coiled tubing welding,” M.Sc. thesis, Xi’an University of Technology, 2011.
7. K. Zhang,“ Research on corrosion resistance of coiled tubing welded joints in sulfur-containing media,” M.Sc. thesis, Xi’an University of Technology, 2011.
8. Research progress in corrosion issue and prevention countermeasures of the coiled tubing for downhole sour services10.3787/j.issn.1000-0976.2011.04.026 ↗
9. Progress on research in the fatigue life of the coiled tubing in sour service
10. Research on the bend fatigue life of the coiled tubing exposed to sour environments
11. Containing corrosion pit limit of coiled tubing corrosion pit depth and residual strength analysis
12. Study on properties test of 3Cr steel high frequency induction welding steel pipe
13. Study on the performance of C90 grade corrosion resistance HFW casing
14. Research on HFW weld performance optimization process
15. Evaluation methods of HFW weld groove corrosion sensitivity
16. Research on test methods of groove corrosion sensitivity for J55 HFW welded pipe
17. J55 HFW oil pipe Luohe water corrosion test research
18. Grooving corrosion behavior of J55 steel-grade casing with electrical resistance welded seam
19. Development of N80 grade HFW casing
20. Effect of different heat treatment technology on grooving corrosion of HFW pipes
21. Research on properties of X65MS low Mn high Nb sour resistance HFW pipe
22. Application of laser confocal scanning microscope in characterization of corrosion morphology
23. Causes of forming corrosion grooves in gas well tubing
24. Study on HFW weld groove corrosion sensitivity by microelectrode scanning method
25. Effect of temperature on electrochemical corrosion behavior of CT80 coiled tubing steel
26. Grooving corrosion of electric resistance welded steel pipe in sea water case histories and effects of alloying elements
27. Influence of oil and gas well environmental factors on grooving corrosion of ERW-OCTG
28. 2019
29. 2015
30. Effect of microstructure and heat-treatment on grooving corrosion of electric resistance welded pipes
31. Grooving corrosion in electric resistance welded steel pipe in sea water10.1016/s0010-938x(78)80076-6 ↗
32. Effect of structure evolution induced by ultrasonic peening on the corrosion behavior of AISI-321 stainless steel10.1016/j.msea.2006.12.049 ↗
33. Influence of nickel additions on the corrosion behaviour of low nitrogen 22% Cr series duplex stainless steels10.1016/j.corsci.2008.05.023 ↗