Superconductivity induced by hydrostatic pressure effect in LaO0.5F0.5Bi(S0.9Se0.1)2

Electrical resistivity of LaO0.5F0.5Bi(S0.9Se0.1)2 have been measured at a temperature range of 2.8 ∼ 300 K by applying several hydrostatic pressures. Pressure-induced superconducting phase was observed above a pressure P of 0.85 GPa and Tc increased from 2.86 K to 8.42 K. The sudden increase of Tc in LaO0.5F0.5Bi(S0.9Se0.1)2 results from the structural phase transition from tetragonal (P4/nmm) to monoclinic (P21/m). Structural phase transition pressure Pc of LaO0.5F0.5Bi(S0.9Se0.1)2 is higher than that of LaO0.5F0.5BiS2. The increase of Pc is ascribed to the suppression of the displacement parameter of the in-plane chalcogen site induced by chemical pressure of Se-substitution.