Radiation enhanced oxidation of proton-irradiated copper thin-films: Towards a new concept of ultra-high radiation dosimetry
Source abstract
Abstract
The effects of extreme radiation levels on the electrical resistivity of metal thin films made of copper were studied by means of electrical measurements and post irradiation imaging. Different 3x3 mm2 chips were produced by depositing 500 nm of meander shaped copper on top of a silicon substrate. A subset of samples was also passivated by sputtering 300 nm of SiO2. During irradiation with 23 GeV protons up to 1.2 x 1017 p/cm2 at the CERN IRRAD Proton Facility, only not-passivated copper samples have shown an increase of resistivity proportional to the particle fluence, indicating that the dominant factor of the resistivity increase is not directly an accumulation of displacement damage, but the radiation enhanced oxidation of the copper film exposed to air. Post-irradiation imaging of the chips cross sections has confirmed the presence of a grown copper oxide film on the surface as well as oxide wells that extended within the bulk following the grain boundaries. This permanent increase of resistance due to radiation enhanced oxidation, can be used for monitoring high energy particles fluence up to levels currently not reachable by standard silicon technology.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Semiconductor materials and devices · Nuclear materials and radiation effects · Ion-surface interactions and analysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
EP-DT-DD, European Organization for Nuclear Research (CERN) 1 , 1211 Geneva, Switzerland
EDLAB, École Polytechnique Fédérale de Lausanne (EPFL) 2 , 1015 Lausanne, Switzerland
CMi, École Polytechnique Fédérale de Lausanne (EPFL) 3 , 1015 Lausanne, Switzerland
Funding
CERN
References (32)
Show source-provided references
1. The behaviour of copper in view of radiation damage in the LHC luminosity upgrade
2. Theory and experimental background on dimensional changes in irradiated alloys10.1016/0022-3115(94)90009-4 ↗
3. Radiation effects in structural materials10.1146/annurev.ms.09.080179.002201 ↗
4. Defects and transmutations in reactor-irradiated copper10.1016/0022-3115(82)90485-8 ↗
5. Nuclear and space radiation effects on materials, NASA Space Vehicle Design Criteria- (Structures)
6. Fundamental aspects of radiation damage in metals
7. 2012 · 65
8. Radiation damage accumulation and associated mechanical hardening in thin films and bulk materials
9. Development and Characterisation of radiation monitoring sensors for the high energy physics experiments of the CERN LHC accelerator
10. Future Circular Collider
11. Evaluation of the radiation field in the future circular collider detector10.1103/physrevaccelbeams.19.111004 ↗
12. Ultrahigh fluence radiation monitoring technology for the future circular collider at CERN10.1109/tns.2018.2797540 ↗
13. Metal Thin-film dosimetry technology for the ultra-high particle fluence environment of the future circular collider at CERN10.21175/radj.2018.03.029 ↗
14. 2019-03-15
15. Electromigration threshold in copper interconnects10.1063/1.1371251 ↗
16. Irradiation Facilities at CERN
17. Single- and multi-foils 27Al(p,3pn)24Na activation technique for monitoring the intensity of high-energy beams10.1016/j.nima.2017.03.058 ↗
18. The temperature coefficient of resistance of copper10.1016/s0016-0032(10)90872-7 ↗
19. Stopping-power and range tables for electrons, protons, and helium ions
20. Formation of very thin oxide films on copper: Kinetics and mechanism10.1007/bf00604475 ↗
21. Oxidation mechanism of Cu2O to CuO at 600-1050 °C10.1007/s11085-004-7808-6 ↗
22. C. Gattinoni and A. Michaelides, “Atomistic details of oxide surfaces and surface oxidation: the example of copper and its oxides,” Surface Science Reports 70, 424–447 (2015), arXiv:1508.01005.10.1016/j.surfrep.2015.07.00110.1016/j.surfrep.2015.07.001 ↗
23. Oxidation mechanism of thin Cu films: A gateway towards the formation of single oxide phase10.1063/1.5028407 ↗
24. Comparison of the oxidation behavior of nanocrystalline and coarse-grain copper10.1007/s11085-005-4381-6 ↗
25. S. Samal, “High-Temperature Oxidation of Metals,” in High Temperature Corrosion, Vol. 12 (InTech, 2016) pp. 11–17, 9809069v1 [arXiv:gr-qc].10.5772/63000 ↗
26. Size-dependent thermal oxidation of copper: Single-step synthesis of hierarchical nanostructures10.1039/c1nr10993f ↗
27. Water radiolysis: Influence of oxide surfaces on H2 production under ionizing radiation10.3390/w3010235 ↗
28. Radiation induced corrosion of copper for spent nuclear fuel storage10.1016/j.radphyschem.2013.06.033 ↗
29. The corrosion of copper in irradiated and unirradiated humid air10.1016/j.corsci.2018.05.024 ↗
30. General relationship for the thermal oxidation of silicon10.1063/1.1713945 ↗
31. Crystallization and electrical resistivity of Cu2O and CuO obtained by thermal oxidation of Cu thin films on SiO2/Si substrates10.1016/j.tsf.2012.06.043 ↗
32. Oxidation-rate excursions during the oxidation of copper in gaseous environments at moderate temperatures10.1023/a:1027331605417 ↗