Intrinsic flux pinning mechanisms in different thickness MgB2 films

MgB2 films in four thickness (60 nm, 200nm, 600nm and 1μm) have been fabricated by hybrid physical–chemical vapor deposition technique (HPCVD). By measuring the magnetization hysteresis loops and the resistivity, we have obtained the transport and magnetic properties of the four films. After that, the pinning mechanisms in them were discussed. Comparing the pinning behaviors in these ultrathin films, thin films and thick films, it was found that there exist different pinning types in MgB2 films of different thickness. In combination with the study of the surface morphology, cross-section and XRD results, we concluded that MgB2 films had different growth modes in different growth stages. For thin films, films grew along c axis, and grain boundaries acted as surface pinning. While for thick films, films grew along c axis at first, and then changed to a-b axis growth. As a result, the a-b axis grains acted as strong volume pinning.