journal article·2017-05-01Open access

Patterning of two-dimensional electron systems in SrTiO3 based heterostructures using a CeO2 template

D. Fuchs, K. Wolff, R. Schäfer, R. Thelen, M. Le Tacon, R. Schneider

AIP Advances· Volume 7· Issue 5

Abstract

Two-dimensional electron systems found at the interface of SrTiO3-based oxide heterostructures often display anisotropic electric transport whose origin is currently under debate. To characterize transport along specific crystallographic directions, we developed a hard-mask patterning routine based on an amorphous CeO2 template layer. The technique allows preparing well-defined microbridges by conventional ultraviolet photolithography which, in comparison to standard techniques such as ion- or wet-chemical etching, does not induce any degradation of interfacial conductance. The patterning scheme is described in detail and the successful production of microbridges based on amorphous Al2O3-SrTiO3 heterostructures is demonstrated. Significant anisotropic transport is observed for T < 30 K which is mainly related to impurity/defect scattering of charge carriers in these heterostructures.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Electronic and Structural Properties of Oxides · Semiconductor materials and devices · Magnetic and transport properties of perovskites and related materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Institut für Festkörperphysik 1 Karlsruher Institut für Technologie, , D-76021 Karlsruhe, Germany

Institut für Mikrostrukturtechnik 2 Karlsruher Institut für Technologie, , D-76021 Karlsruhe, Germany

References (22)

Show source-provided references
1. Nature · 2002 · 419 · 37810.1038/nature00977 ↗
2. Nature · 2004 · 427 · 42310.1038/nature02308 ↗
3. Science · 2007 · 317 · 119610.1126/science.1146006 ↗
4. Nature Mater. · 2013 · 12 · 54210.1038/nmat3624 ↗
5. Nat. Mater. · 2007 · 6 · 49310.1038/nmat1931 ↗
6. Phys. Rev. Lett. · 2010 · 104 · 12680310.1103/PhysRevLett.104.126803 ↗
7. Phys. Rev. B · 2010 · 81 · 15341410.1103/PhysRevB.81.153414 ↗
8. Appl. Phys. Lett. · 2014 · 105 · 09260210.1063/1.4895120 ↗
9. Phys. Rev. B · 2012 · 86 · 060503(R)10.1103/physrevb.86.060503 ↗
10. Nature Phys. · 2011 · 7 · 76210.1038/nphys2080 ↗
11. Nature Commun. · 2011 · 2 · 18810.1038/ncomms1192 ↗
12. Nature Mater. · 2013 · 12 · 109110.1038/nmat3753 ↗
13. Nature Mater. · 2013 · 12 · 111210.1038/nmat3810 ↗
14. Phys. Rev. Lett. · 2012 · 108 · 16680210.1103/PhysRevLett.108.166802 ↗
15. Phys. Rev. B · 2016 · 93 · 18450410.1103/PhysRevB.93.184504 ↗
16. Appl. Phys. Lett. · 2015 · 107 · 19160410.1063/1.4935553 ↗
17. Appl. Phys. Lett. · 1998 · 73 · 292010.1063/1.122630 ↗
18. Adv. Electron. Mater. · 2015 · 1 · 150011410.1002/aelm.201500114 ↗
19. Phys. Rev. B · 2015 · 92 · 15531310.1103/PhysRevB.92.155313 ↗
20. Cryst. Eng. Comm. · 2014 · 16 · 173510.1039/c3ce42037j ↗
21. Phys. Rev. Lett. · 2001 · 87 · 08550510.1103/physrevlett.87.085505 ↗
22. Appl. Phys. Lett. · 2011 · 98 · 24290410.1063/1.3600339 ↗