Effect of magnetic field annealing on soft magnetic properties of Co71Fe2Si14-xB9+xMn4 amorphous alloys with low permeability

The effect of transverse magnetic field annealing (TFA) on soft magnetic properties of Co71Fe2Si14-xB9+xMn4 amorphous alloys was investigated with the aim of reducing effective permeability (μe). It was revealed that the increasing B content improved thermal stability, increased saturation magnetic flux density (Bs) of as-quenched alloys, while the samples exhibited a slightly larger coercivity (Hc) when the atom percentages of Si and B were similar. Permeability decreased dramatically after TFA. The decrease of permeability mainly depended on annealing temperature and magnetic field intensity. Besides, flat hysteresis loops were obtained after TFA, Lorentz micrograph observation revealed the TFA sample exhibited denser magnetic domain walls, which confirmed it was more difficult to be saturated. The Co71Fe2Si9B14Mn4 alloy was successful prepared with low μe of 3020, low Hc of 1.7 A/m and high resistance to DC bias 6 times that of as-quenched alloy at the DC field of 300 A/m.