Ga-, Y-, and Sc-substituted M-type ferrites for self-biasing circulators in LTCC microwave modules

Manuel Heidenreich, Xinyi Ma, Wanja Gitzel, Arne Jacob, Beate Capraro, Jörg Töpfer

AIP Advances· Volume 10· Issue 2

Abstract

The partial substitution of Fe3+ by diamagnetic Me3+ in BaMexFe12-xO19 with Me = Ga and Y (0 ≤ x ≤ 2) was studied. Samples were synthesized by the mixed-oxide route and their properties were compared to BaScxFe12-xO19 ferrites. It was shown by XRD that the hexagonal lattice parameters with x for Me = Ga and Sc vary continuously. For Me = Y no single-phase ferrites were obtained indicating that the solubility limit for Y in Ba ferrite is very limited. For Me = Ga and Sc, the saturation magnetization at room temperature is reduced with x. The coercivity as well as the ferromagnetic resonance frequency remain almost unchanged for Ga-substituted ferrites, whereas for Sc-substituted ferrites the coercivity and ferromagnetic resonance frequency decrease with x. Thick films of Sc-ferrite (x = 0.5) were screen-printed onto LTCC tape substrates and post-fired at 900°C. Application of a magnetic field during drying allows fabrication of textured ferrite layers. Alternatively, ferrite tapes and LTCC tapes were successfully co-fired at 900°C.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Magnetic Properties and Synthesis of Ferrites · Multiferroics and related materials · Magneto-Optical Properties and Applications

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Ernst-Abbe-Hochschule Jena 1 , 07745 Jena, Germany

Hamburg University of Technology 2 , 21073 Hamburg, Germany

Fraunhofer IKTS 3 , 07629 Hermsdorf, Germany

Funding

Deutsches Zentrum für Luft- und Raumfahrt

References (21)

Show source-provided references
1. J. Magn. Magn. Mater. · 2000 · 215-216 · 17110.1016/s0304-8853(00)00106-2 ↗
2. J. Mater. Sci. Mater. Electron. · 2009 · 20 · 78910.1007/s10854-009-9923-2 ↗
3. J. Magn. Magn. Mater. · 2009 · 321 · 203510.1016/j.jmmm.2009.01.004 ↗
4. J. Appl. Phys. · 2006 · 99 · 08M91110.1063/1.2165145 ↗
5. J. Appl. Phys. · 2000 · 87 · 498110.1063/1.373222 ↗
6. Wohlfahrt · 1982 · 305
7. 1961
8. J. Appl. Phys. · 1967 · 38 · 531510.1063/1.1709321 ↗
9. Mat. Res. Bull. · 1984 · 19 · 38510.1016/0025-5408(84)90181-8 ↗
10. J. Appl. Phys. · 1991 · 70 · 614010.1063/1.350022 ↗
11. Mat. Res. Bull. · 2017 · 86 · 1910.1016/j.materresbull.2016.09.025 ↗
12. Sov. Phys. JETP · 1970 · 31 · 840
13. J. Magn. Magn.Mater. · 2017 · 442 · 30010.1016/j.jmmm.2017.06.022 ↗
14. J.Mater. Sci. Mater. Electr. · 2019 · 30 · 591110.1007/s10854-019-00889-x ↗
15. J. Europ. Ceram. Soc. · 2019 · 39 · 307710.1016/j.jeurceramsoc.2019.04.014 ↗
16. Solid State Phenomena · 2010 · 160 · 6310.4028/www.scientific.net/ssp.160.63 ↗
17. Acta Cryst. A · 1976 · 32 · 75110.1107/s0567739476001551 ↗
18. Appl. Phys. A · 1981 · 26 · 4510.1007/bf01197677 ↗
19. J. Magn. Magn. Mater. · 2009 · 321 · 404510.1016/j.jmmm.2009.07.088 ↗
20. J. Appl. Phys. · 1999 · 85 · 522910.1063/1.369952 ↗
21. J. Appl. Phys. · 2009 · 105 · 02390810.1063/1.3067759 ↗