Structure and properties of sintered MM–Fe–B magnets

R. X. Shang, J. F. Xiong, R. Li, W. L. Zuo, J. Zhang, T. Y. Zhao, R. J. Chen, J. R. Sun, B. G. Shen

AIP Advances· Volume 7· Issue 5

Abstract

MM14Fe79.9B6.1 magnets were prepared by conventional sintering method. The Curie temperature of the sintered MM2Fe14B magnet was about 210 °C. When the sintering temperature increased from 1010 °C to 1030 °C, the density of the magnet increased from 6.85 g/cm3 to 7.52 g/cm3. After the first stage tempering at 900 °C, the (BH)max and Hcj had a slight increase. The maximum value of (BH)max = 7.6 MGOe and Hcj = 1080 Oe was obtained when sintered at 1010 °C and tempering at 900 °C, respectively. The grain size grew very large when the sintering temperature increased to 1050 °C, and the magnetic properties deteriorated rapidly. La reduced by ∼ 7.5 at. % in grains, which is almost equal to the increased percentage of Nd. That is mainly because La-Fe-B is very difficult to form the 2: 14: 1 phase.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Magnetic Properties of Alloys · Rare-earth and actinide compounds · Magnetic properties of thin films

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Chinese Academy of Sciences 1 State Key Laboratory of Magnetism, Institute of Physics, , Beijing 100190, P. R. China

University of Chinese Academy of Sciences 2 , Beijing 100049, P. R. China

Chinese Academy of Sciences 3 Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Materials Technology and Engineering, , Ningbo 315201, P. R. China

Funding

the Knowledge Innovation Project of the Chinese Academy of Sciences · the National Key Research Program of China · the National Natural Science Foundation of China

References (18)

Show source-provided references
1. J. Alloys Compd. · 2015 · 651 · 14410.1016/j.jallcom.2015.08.044 ↗
2. J. Alloys Compd. · 2015 · 628 · 32510.1016/j.jallcom.2014.12.042 ↗
3. J. Magn. Magn. Mater. · 2016 · 399 · 2610.1016/j.jmmm.2015.09.051 ↗
4. J. Appl. Phys. · 1988 · 63 · 351310.1063/1.340726 ↗
5. J. Magn. Magn. Mater. · 2002 · 248 · 44110.1016/S0304-8853(02)00335-9 ↗
6. J. Phys. D: Appl. Phys. · 2000 · 33 · 21710.1088/0022-3727/33/22/201 ↗
7. J. Phys.: Condens. Matter · 2004 · 16 · 45510.1088/0953-8984/16/5/007 ↗
8. J. Phys. D: Appl. Phys. · 2011 · 44 · 06400110.1088/0022-3727/44/6/064001 ↗
9. J. Magn. Magn. Mater. · 1997 · 176 · 31310.1016/S0304-8853(97)00652-5 ↗
10. Phys. Rev. B · 1984 · 29 · 417610.1103/PhysRevB.29.4176 ↗
11. Phys. Rev. B · 2014 · 89 · 23512610.1103/PhysRevB.89.235126 ↗
12. Rep. Prog. Phys. · 1998 · 61 · 109910.1088/0034-4885/61/9/001 ↗
13. J. Appl. Phys. · 1986 · 59 · 87310.1063/1.336611 ↗
14. J. Phys.: Conf. Ser. · 2011 · 266 · 01205210.1088/1742-6596/266/1/012052 ↗
15. Mater. Chem. Phys. · 2001 · 67 · 27210.1016/S0254-0584(00)00450-8 ↗
16. J. Magn. Magn. Mater. · 2015 · 382 · 2610.1016/j.jmmm.2015.01.043 ↗
17. Can. J. Phys. · 1987 · 65 · 120010.1139/p87-196 ↗
18. Rare Metal Mat. Eng. · 2015 · 44 · 748