journal article·2013-03-01Open access

Roles of hydrogenation, annealing and field in the structure and magnetic entropy change of Tb-based bulk metallic glasses

Qiang Luo, Björn Schwarz, Norbert Mattern, Jun Shen, Jürgen Eckert

AIP Advances· Volume 3· Issue 3

Abstract

The reduction of open-volume regions in Tb-based metallic glass (MG) by annealing and hydrogen charging was found to rearrange the atomic structure and tune the magnetic behaviors. After crystallization, the magnetic structure and magnetic entropy change (MEC) alters due to the structural transformation, and a plateau-like-MEC behavior can be obtained. The hydrogen concentration after charging at 1mA/cm2 for 576 h reaches as high as 3290 w-ppm. The magnetization behavior and the MEC change due to the modification of the exchange interaction and the random magnetic anisotropy (RMA) upon hydrogenation. At low temperatures, irreversible positive MEC was obtained, which is related to the internal entropy production. The RMA-to-exchange ratio acts as a switch to control the irreversible entropy production channel and the reversible entropy transfer channel. The field dependence of the MEC is discussed in term of the competition among Zeeman energy, exchange interaction and RMA.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Metallic Glasses and Amorphous Alloys · Theoretical and Computational Physics · Magnetic and transport properties of perovskites and related materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Tongji University 1 School of Materials Science and Engineering, , Shanghai 201804, P. R. China

Institute for Complex Materials 2 IFW Dresden, , Helmholtzstr. 20, D-01069 Dresden, Germany

Institute of Materials Science 3 TU Dresden, , D-01062 Dresden, Germany

References (32)

Show source-provided references
1. Rep. Prog. Phys. · 2005 · 68 · 147910.1088/0034-4885/68/6/R04 ↗
2. Nature · 2004 · 429 · 85310.1038/nature02657 ↗
3. Acta. Mater. · 2011 · 59 · 41210.1016/j.actamat.2010.09.059 ↗
4. Phys. Rev. B · 2003 · 67 · 10441610.1103/PhysRevB.67.104416 ↗
5. Acta. Mater. · 2011 · 59 · 360210.1016/j.actamat.2011.02.033 ↗
6. J Non-Cryst. Solids · 2009 · 355 · 75910.1016/j.jnoncrysol.2009.02.006 ↗
7. J. Alloys. Compd. · 2010 · 495 · 20910.1016/j.jallcom.2010.01.125 ↗
8. J. Magn. Magn. Mater. · 2010 · 322 · 229810.1016/j.jmmm.2010.02.029 ↗
9. J. Appl. Phys. · 2011 · 109 · 07A93310.1063/1.3561447 ↗
10. Solid State Commun · 2008 · 145 · 1510.1016/j.ssc.2007.10.007 ↗
11. Appl. Phys. Lett. · 2009 · 94 · 11250710.1063/1.3097237 ↗
12. Phys. Rev. B · 2010 · 82 · 02420410.1103/PhysRevB.82.024204 ↗
13. Alefeld · 1978 · 16910.1007/3-540-08705-2 ↗
14. Intermetallics · 2002 · 10 · 120710.1016/S0966-9795(02)00134-6 ↗
15. J. Alloys. Compd. · 2000 · 298 · 14610.1016/S0925-8388(99)00617-9 ↗
16. Mater. Res. Soc. Symp. Proc. · 1999 · 553 · 4910.1557/PROC-553-49 ↗
17. Mater. Sci. Eng. A · 2009 · 521-522 · 35410.1016/j.msea.2008.10.078 ↗
18. Appl. Phys. Lett. · 2003 · 83 · 113410.1063/1.1600836 ↗
19. J Non-Cryst Solids · 2005 · 351 · 237310.1016/j.jnoncrysol.2005.07.012 ↗
20. Appl. Phys. Lett. · 2006 · 88 · 13250910.1063/1.2188385 ↗
21. J. Magn. Magn. Mater. · 2006 · 304 · 64210.1016/j.jmmm.2006.02.156 ↗
22. J. Appl. Phys. · 2007 · 101 · 09390310.1063/1.2724804 ↗
23. J. Appl. Phys. · 1987 · 62 · 387310.1063/1.339232 ↗
24. J. Appl. Phys. · 1992 · 72 · 110.1063/1.352158 ↗
25. Sov. Tech. Phys. Lett. · 1991 · 17 · 353
26. J. Appl. Phys. · 1997 · 81 · 82410.1063/1.364166 ↗
27. J. Appl. Phys. · 1984 · 55 · 433410.1063/1.333046 ↗
28. J. Alloys Compd. · 2000 · 314 · 17010.1016/S0925-8388(00)01211-1 ↗
29. Appl. Phys. Lett. · 2009 · 95 · 24190110.1063/1.3266521 ↗
30. Bambakides · 1981 · 2110.1007/978-1-4757-5814-6 ↗
31. J. Appl. Phys. · 1984 · 55 · 180010.1063/1.333483 ↗
32. J. Appl. Phys. · 1982 · 53 · 779810.1063/1.330166 ↗