Regulation of oxygen vacancy types on SnO2 (110) surface by external strain

Z. H. Zhou, Y. M. Min, X. X. Liu, J. Q. Ding, J. H. Guo, F. R. Hu, L. Z. Liu

AIP Advances· Volume 6· Issue 5

Abstract

In tin dioxide nanostructures, oxygen vacancies (OVs) play an important role in their optical properties and thus regulation of both OV concentration and type via external strain is crucial to exploration of more applications. First-principle calculations of SnO2 (110) surface disclose that asymmetric deformations induced by external strain not only lead to its intrinsic surface elastic changes, but also result in different OV formation energy. In the absence of external strain, the energetically favorable oxygen vacancies(EFOV) appear in the bridging site of second layer. When -3.5% external strain is applied along y direction, the EFOV moves into plane site. This can be ascribed that the compressed deformation gives rise to redistribution of electronic wave function near OVs, therefore, formation of newly bond structures. Our results suggest that different type OVs in SnO2 surface can be controlled by strain engineering.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: ZnO doping and properties · Gas Sensing Nanomaterials and Sensors · Ga2O3 and related materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Nanjing University 1 Nanjing National Laboratory of Microstructures and Department of Physics, , Nanjing 210093, China

Nanjing University of posts and telecommunicates 2 School of Optoelectronic Engineering and Grüenberg Research Centre, , Nanjing 210023, China

Funding

National Natural Science Foundation of China

References (23)

Show source-provided references
1. Phys. Rev.B · 2006 · 73 · 07340610.1103/PhysRevB.73.073406 ↗
2. Nano. Lett. · 2009 · 9 · 192610.1021/nl900075f ↗
3. Appl. Phys. Lett. · 2006 · 88 · 08310510.1063/1.2166695 ↗
4. Science · 2001 · 293 · 26910.1126/science.1061051 ↗
5. Phys. Rev. B · 2005 · 72 · 03540410.1103/PhysRevB.72.035404 ↗
6. Phys. Rev. Lett. · 2002 · 88 · 09550110.1103/PhysRevLett.88.095501 ↗
7. Appl. Phys. Lett. · 2012 · 100 · 12190310.1063/1.3696044 ↗
8. J. Phys. Chem. Solids · 1974 · 35 · 93110.1016/S0022-3697(74)80102-2 ↗
9. Solid Stat Commun. · 1980 · 33 · 34110.1016/0038-1098(80)91166-7 ↗
10. J. Cryst. Growth · 2008 · 311 · 15210.1016/j.jcrysgro.2008.10.072 ↗
11. Adv. Funct. Mater. · 2003 · 13 · 43910.1002/adfm.200304334 ↗
12. App. Phys. Lett. · 2004 · 13 · 174510.1063/1.1655693 ↗
13. App. Phys. Lett. · 2006 · 88 · 18311210.1063/1.2201617 ↗
14. App. Phys. Lett. · 2011 · 99 · 25190210.1063/1.3670337 ↗
15. J. Raman. Spectra. · 2012 · 43 · 142310.1002/jrs.4078 ↗
16. App. Phys. Lett. · 2013 · 102 · 03191610.1063/1.4789538 ↗
17. J. Comput. Phys. · 1997 · 131 · 23310.1006/jcph.1996.5612 ↗
18. Phys. Rev. B · 2001 · 64 · 07540710.1103/PhysRevB.64.075407 ↗
19. Phys. Rev. Lett. · 2004 · 93 · 01610210.1103/PhysRevLett.93.016102 ↗
20. Modell. Simul. Mater. Sci. Eng. · 1992 · 1 · 3910.1088/0965-0393/1/1/004 ↗
21. J.Phys. Chem.B. · 1999 · 103 · 1064410.1021/jp9905528 ↗
22. App. Phys. Lett. · 2004 · 84 · 90910.1063/1.1646460 ↗
23. Phys. Rev. Lett. · 2011 · 106 · 03990210.1103/PhysRevLett.106.039902 ↗