Thermoelectric properties of high pressure synthesized lithium and calcium double-filled CoSb3
Source abstract
Abstract
Lithium and calcium are inefficient filling elements of CoSb3 at ambient pressure, but show nice filling behavior under high pressure. In this work, we synthesized Li/Ca double-filled CoSb3 with high pressure synthesis method. The products show the skutterudite structure of Im3¯ symmetry. Thermoelectric properties were effectively enhanced through Li and Ca co-filling. For the optimal Li0.08Ca0.18Co4Sb12 sample, the power factor maintains a relatively high value over the whole measurement temperature range and peaks at 4700μWm−1K−2, meanwhile the lattice thermal conductivity is greatly suppressed, leading to a maximal ZT of 1.18 at 700 K. Current work demonstrates high pressure synthesis as an effective method to produce multiple elemental filled CoSb3 skutterudites.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced Thermoelectric Materials and Devices · Chalcogenide Semiconductor Thin Films · Thermal properties of materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Yanshan University State Key Laboratory of Metastable Materials Science and Technology, , Qinhuangdao, Hebei 066004, China
Funding
National Natural Science Foundation of China · Natural Science Foundation of Hebei Province
References (27)
Show source-provided references
1. Rowe · 1995 · 407
2. RSC Adv · 2015 · 5 · 4165310.1039/C5RA03942H ↗
3. Science · 1996 · 272 · 132510.1126/science.272.5266.1325 ↗
4. J. Appl. Phys. · 2001 · 90 · 186410.1063/1.1388162 ↗
5. Appl Phys Lett · 2006 · 89 · 22110710.1063/1.2397538 ↗
6. J Am Chem Soc · 2011 · 133 · 783710.1021/ja111199y ↗
7. Acta Mater · 2014 · 63 · 3010.1016/j.actamat.2013.09.039 ↗
8. Acta Mater · 2015 · 95 · 20110.1016/j.actamat.2015.05.024 ↗
9. Proc Natl Acad Sci USA · 2015 · 112 · 326910.1073/pnas.1424388112 ↗
10. Proc Natl Acad Sci USA · 2015 · 112 · 820510.1073/pnas.1510231112 ↗
11. Phys Rev Lett · 2005 · 95 · 18550310.1103/PhysRevLett.95.185503 ↗
12. Phys Rev B · 2006 · 74 · 15320210.1103/PhysRevB.74.153202 ↗
13. Acta Mater · 2008 · 56 · 173310.1016/j.actamat.2007.12.012 ↗
14. Phys Rev B · 2008 · 77 · 04520210.1103/PhysRevB.77.045202 ↗
15. Mater Trans · 2004 · 45 · 310210.2320/matertrans.45.3102 ↗
16. Annu Rev Mater Sci · 1998 · 28 · 63110.1146/annurev.matsci.28.1.631 ↗
17. J Appl Phys · 2013 · 113 · 11370310.1063/1.4795599 ↗
18. Mater Lett · 2013 · 98 · 17110.1016/j.matlet.2013.02.034 ↗
19. Acta Mater · 2012 · 60 · 124610.1016/j.actamat.2011.10.059 ↗
20. J Alloys Compd · 2014 · 615 · 17710.1016/j.jallcom.2014.06.198 ↗
21. J Alloys Compd · 2010 · 493 · 53510.1016/j.jallcom.2009.12.150 ↗
22. J Alloys Compd · 2016 · 677 · 6110.1016/j.jallcom.2016.03.239 ↗
23. Mater Lett · 2011 · 65 · 158210.1016/j.matlet.2011.02.062 ↗
24. Funct Mater Lett · 2015 · 09 · 165000810.1142/S1793604716500089 ↗
25. J Appl Phys · 2004 · 95 · 485210.1063/1.1688463 ↗
26. Appl Phys Lett · 2011 · 98 · 07210910.1063/1.3557068 ↗
27. J Appl Phys · 2002 · 91 · 369810.1063/1.1450036 ↗