Preparation of submicron-sized Sm2Fe17N3 fine powder by ultrasonic spray pyrolysis-hydrogen reduction (USP-HR) and subsequent reduction–diffusion process
Source abstract
Abstract
A new reduction–diffusion method for preparing submicron-sized Sm2Fe17N3 was developed. First, submicron-sized α-Fe/Sm2O3 composite precursors with good dispersibility were prepared directly by ultrasonic spray pyrolysis and hydrogen reduction (USP-HR). Then, the precursor was successfully converted into Sm2Fe17N3 powder by Ca reduction–diffusion and nitridation. The results displayed that the precursor prepared by USP-HR was a monodisperse homogeneous composite of spherical particles of α-Fe and Sm2O3. α-Fe and Sm2O3 exist in an intercalated structure in the composite spherical particles. This creates conditions for the preparation of ultrafine Sm2Fe17N3 particles with uniform sizes and dispersity. The results show that Sm2Fe17N3 is a single-phase, composed of submicron-sized particles with no other impurity phases. The physical property measurement system shows that the coercivity of 0.616 ± 0.347 µm particles reaches 14.7 kOe.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Magnetic Properties of Alloys · Advancements in Battery Materials · Magnetic and transport properties of perovskites and related materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Research Center of Magnetic and Electronic Materials, College of Materials Science and Engineering, Zhejiang University of Technology 1 , Hangzhou 310014, China
Sunny Photoelectric Information Co., Ltd. 2 , Ningbo 315201, China
State Key Laboratory of Rare Earth Permanent Magnet Materials, Earth-Panda Advance Magnetic Material Co., Ltd. 3 , Hefei 231500, China
Funding
State Key Laboratory of Rare Earth Permanent Magnetic Materials · National Natural Science Foundation of China · Zhejiang Xinmiao Talents Program
References (22)
Show source-provided references
1. Preparation of submicron-sized Sm2Fe17N3 fine powder with high coercivity by reduction–diffusion process10.1016/j.jallcom.2016.10.306 ↗
2. Improved magnetic properties by treatment of iron-based rare earth intermetallic compounds in ammonia10.1016/0304-8853(90)90756-g ↗
3. Magnetic properties of sintered Sm2Fe17Ny magnets10.1063/1.355258 ↗
4. Effect of nitrogen content on magnetic properties of Sm2Fe17Nx(0 < x < 6)10.1109/20.179482 ↗
5. Dependence of coercivity on particle size in Sm2Fe17N3 powders10.1016/0925-8388(94)04902-5 ↗
6. Magnetic properties of the single magnetic domain particles of Sm2Fe17Nx compounds10.1016/0925-8388(93)90357-s ↗
7. Sm2Fe17N3 magnet powder made by reduction and diffusion method10.1109/20.800512 ↗
8. Investigation of optimal route to fabricate submicron-sized Sm2Fe17 particles with reduction–diffusion method10.1063/1.4944077 ↗
9. Direct preparation of submicron-sized Sm2Fe17 ultra-fine powders by reduction–diffusion technique10.1016/j.jallcom.2015.12.124 ↗
10. Advances in nanostructures fabricated via spray pyrolysis and their applications in energy storage and conversion10.1039/c8cs00904j ↗
11. Aerosol synthesis of nano-crystalline iron particles from iron (II) chloride solution
12. Fluxmetric and magnetometric demagnetizing factors for cylinders10.1016/j.jmmm.2006.02.235 ↗
13. Synthesis and characterization of nickel particles by hydrogen reduction assisted ultrasonic spray pyrolysis (USP-HR) method10.14356/kona.2011016 ↗
14. Synthesis of nano-crystalline spherical cobalt–iron (Co–Fe) alloy particles by ultrasonic spray pyrolysis and hydrogen reduction10.1016/j.jallcom.2009.03.046 ↗
15. Nanocrystalline spherical iron–nickel (Fe–Ni) alloy particles prepared by ultrasonic spray pyrolysis and hydrogen reduction (USP-HR)10.1016/j.jallcom.2009.01.094 ↗
16. Iron-nickelcobalt (Fe-Ni-Co) alloy particles prepared by ultrasonic spray pyrolysis and hydrogen reduction (USP-HR) method10.1002/9781118744109.ch27 ↗
17. Synthesis, structural and magnetic characterization of soft magnetic nanocrystalline ternary FeNiCo particles10.1016/j.jmmm.2016.09.005 ↗
18. Magnetic and porous nanospheres from ultrasonic spray pyrolysis10.1021/ja050693p ↗
19. Synthesis and magnetic properties of Sm2Co17 particles using salt-assisted spray pyrolysis and a reduction-diffusion process10.1016/j.apsusc.2019.01.030 ↗
20. High coercivity Sm2Fe17N3 submicron size powder prepared by polymerized-complex and reduction–diffusion process10.1016/j.scriptamat.2016.03.028 ↗
21. Corrosion mechanism of H2O on Sm2Fe17 and nitrogenation process of corroded Sm2Fe1710.1016/j.jre.2018.10.015 ↗
22. Synthesis mechanism of Sm2Fe17 alloy produced in reduction-diffusion process10.1016/s1002-0721(10)60357-2 ↗