Polycrystalline Terfenol-D thin films grown at CMOS compatible temperature

Mohanchandra K. Panduranga, Taehwan Lee, Andres Chavez, Sergey V. Prikhodko, Gregory P. Carman

AIP Advances· Volume 8· Issue 5

Abstract

Terfenol-D thin films have the largest magnetoelastic coefficient at room temperature of any material system and thus are ideal for voltage induced strain multiferroics. However, Terfenol-D requires 500 0C processing temperature which prohibits its use in CMOS devices where processing temperatures must be below 450 0C. In this paper, we describe a deposition process that produces quality Terfenol-D film with processing temperature below 450 0C. These films have extremely smooth surfaces (Ra∼1nm) with excellent magnetoelastic properties (λs=880 microstrain) similar to its bulk polycrystalline counterpart. The films are produced by DC magnetron sputtering and deposited on heated substrates at 250 0C and post annealed at either 250 0C, 400 0C or 450 0C. Among these films only the film annealed at 450 0C produces crystalline Terfenol-D with a face centered cubic crystal structure and saturation magnetization of ∼700 emu/cc. MOKE Magnetic hysteresis loops measured with four point bending fixture show compressive strain dramatically alter the coercive field from 2300 Oe to 1600 Oe.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Multiferroics and related materials · Magnetic Properties and Applications · Magnetic properties of thin films

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Department of Mechanical and Aerospace Engineering, University of California 1 , Los Angeles, CA 90095, USA

Department of Materials Science and Engineering, University of California 2 , Los Angeles, CA 90095, USA

Funding

STARnet · NSF | ENG | Division of Engineering Education and Centers

References (20)

Show source-provided references
1. J. Appl. Phys. Part 1 · 2001 · 40 · 494810.1143/jjap.40.4948 ↗
2. J. Alloys and Compounds · 2014 · 590 · 4610.1016/j.jallcom.2013.12.065 ↗
3. Phil. Trans. R. Soc. A · 2014 · 372 · 2012043910.1098/rsta.2012.0439 ↗
4. J. Phys. D, Appl. Phys. · 2011 · 44 · 34300110.1088/0022-3727/44/24/243001 ↗
5. Appl. Phys. Lett. · 2006 · 88 · 18250210.1063/1.2199967 ↗
6. Phys. Rev. B · 2009 · 80 · 05410210.1103/physrevb.80.054102 ↗
7. Appl. Phys. Lett. · 2013 · 102 · 02290610.1063/1.4775764 ↗
8. J. Appl. Phys. · 1997 · 81 · 569610.1063/1.364871 ↗
9. J. Appl. Phys. · 1994 · 76 · 700010.1063/1.358068 ↗
10. J Nano R · 2012 · 18-19 · 23510.4028/www.scientific.net/jnanor.18-19.235 ↗
11. J. Appl. Phys. · 1994 · 76 · 538010.1063/1.357192 ↗
12. Sensors and Actuators A · 2003 · 106 · 29810.1016/s0924-4247(03)00188-2 ↗
13. J. Appl. Phys. · 1994 · 75 · 525710.1063/1.355724 ↗
14. AIP Advances · 2015 · 5 · 09711910.1063/1.4930602 ↗
15. Phys. Rev. B. · 2016 · 93 · 06442510.1103/physrevb.93.064425 ↗
16. Appl. Phy. Lett. · 2011 · 98 · 12310310.1063/1.3569142 ↗
17. Meas. Sci. Technol. · 2013 · 24 · 04560110.1088/0957-0233/24/4/045601 ↗
18. Math. Phys. · 1918 · 2 · 98
19. 2000
20. Strain-induced magnetization change in patterned ferromagnetic nickel nanostructures10.1063/1.3592344 ↗