High pressure synthesis of amorphous TiO2 nanotubes
Source abstract
Abstract
Amorphous TiO2 nanotubes with diameters of 8-10 nm and length of several nanometers were synthesized by high pressure treatment of anatase TiO2 nanotubes. The structural phase transitions of anatase TiO2 nanotubes were investigated by using in-situ high-pressure synchrotron X-ray diffraction (XRD) method. The starting anatase structure is stable up to ∼20GPa, and transforms into a high-density amorphous (HDA) form at higher pressure. Pressure-modified high- to low-density transition was observed in the amorphous form upon decompression. The pressure-induced amorphization and polyamorphism are in good agreement with the previous results in ultrafine TiO2 nanoparticles and nanoribbons. The relationship between the LDA form and α-PbO2 phase was revealed by high-resolution transmission electron microscopy (HRTEM) study. In addition, the bulk modulus (B0 = 158 GPa) of the anatase TiO2 nanotubes is smaller than those of the corresponding bulks and nanoparticles (180-240 GPa). We suggest that the unique open-ended nanotube morphology and nanosize play important roles in the high pressure phase transition of TiO2 nanotubes.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Diamond and Carbon-based Materials Research · Boron and Carbon Nanomaterials Research · Transition Metal Oxide Nanomaterials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Jilin University 1 State Key Laboratory of Superhard Materials, , Changchun 130012, China
Institute of High Energy Physics 2 , Chinese Academy of Sciences, Beijing 100049, China
Funding
Cheung Kong Scholars Programme of China · Consortium for Materials Properties Research in Earth Sciences under NSF Cooperative Agreement EAR · National Basic Research Progran of China · National Natural Science Foundation of China
References (29)
Show source-provided references
1. Science · 1999 · 284 · 134010.1126/science.284.5418.1340 ↗
2. Chem. Rev. · 2006 · 106 · 110510.1021/cr050569o ↗
3. Angew. Chem. Int. Ed. · 2011 · 50 · 2909
4. J. Phys. Chem. C · 2007 · 111 · 614310.1021/jp0702595 ↗
5. ACS Appl. Mater. Interfaces · 2014 · 6 · 2219910.1021/am505893q ↗
6. J. Mater. Chem. · 2007 · 17 · 145110.1039/b701168g ↗
7. Nano Lett. · 2006 · 6 · 21510.1021/nl052099j ↗
8. ACS Catal. · 2012 · 2 · 94910.1021/cs200621c ↗
9. J. Mater. Chem. A · 2015 · 11 · 588210.1039/C4TA07190E ↗
10. Nanoscale · 2014 · 10 · 524510.1039/c3nr06736j ↗
11. Nature · 2013 · 493 · 38510.1038/nature11728 ↗
12. Nature · 2014 · 510 · 25010.1038/nature13381 ↗
13. J. Phys. Chem. Lett. · 2010 · 1 · 30910.1021/jz9001828 ↗
14. J. Phys. Chem. C · 2013 · 117 · 851610.1021/jp4004196 ↗
15. RSC Adv. · 2014 · 4 · 1287310.1039/c3ra46404k ↗
16. J. Phys. Chem. C · 2013 · 117 · 850310.1021/jp312705u ↗
17. Nano Lett. · 2013 · 8 · 372910.1021/nl4016705 ↗
18. Phys. Rev. Lett. · 2010 · 105 · 09570110.1103/PhysRevLett.105.095701 ↗
19. Phys. Rev. Lett. · 2006 · 96 · 13570210.1103/PhysRevLett.96.135702 ↗
20. Phys. Rev. B · 2004 · 70 · 13410210.1103/PhysRevB.70.134102 ↗
21. Phys. Rev. Lett. · 2009 · 103 · 07550510.1103/PhysRevLett.103.075505 ↗
22. Physica B. · 2014 · 445 · 4210.1016/j.physb.2014.03.079 ↗
23. J. Appl. Crystallogr. · 2001 · 34 · 21010.1107/S0021889801002242 ↗
24. Catal. Today · 2011 · 166 · 1810.1016/j.cattod.2010.03.045 ↗
25. Phys. Rev. B · 2000 · 6 · 1441410.1103/PhysRevB.61.14414 ↗
26. J. Phys. Chem. C · 2008 · 112 · 962710.1021/jp801555a ↗
27. Solid State Comm. · 2003 · 125 · 11110.1016/S0038-1098(02)00601-4 ↗
28. Phys. Rev. Lett. · 2006 · 96 · 03550910.1103/PhysRevLett.96.035509 ↗
29. Can. J. Chem. · 2015 · 93 · 16510.1139/cjc-2014-0241 ↗