Tuning the carrier concentration to improve the thermoelectric performance of CuInTe2 compound
Source abstract
Abstract
The electronic and transport properties of CuInTe2 chalcopyrite are investigated using density functional calculations combined with Boltzmann theory. The band gap predicted from hybrid functional is 0.92 eV, which agrees well with experimental data and leads to relatively larger Seebeck coefficient compared with those of narrow-gap thermoelectric materials. By fine tuning the carrier concentration, the electrical conductivity and power factor of the system can be significantly optimized. Together with the inherent low thermal conductivity, the ZT values of CuInTe2 compound can be enhanced to as high as 1.72 at 850 K, which is obviously larger than those measured experimentally and suggests there is still room to improve the thermoelectric performance of this chalcopyrite compound.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced Thermoelectric Materials and Devices · Chalcogenide Semiconductor Thin Films · Copper-based nanomaterials and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Wuhan University Key Laboratory of Artificial Micro- and Nano-structures of Ministry of Education and School of Physics and Technology, , Wuhan 430072, China
References (33)
Show source-provided references
1. Nature · 2011 · 473 · 6610.1038/nature09996 ↗
2. Nat. Mater. · 2012 · 11 · 42210.1038/nmat3273 ↗
3. Nature · 2008 · 451 · 16310.1038/nature06381 ↗
4. Science · 2008 · 321 · 55410.1126/science.1159725 ↗
5. Science · 1996 · 272 · 132510.1126/science.272.5266.1325 ↗
6. Nature · 2012 · 489 · 41410.1038/nature11439 ↗
7. Science · 2004 · 303 · 81810.1126/science.1092963 ↗
8. Nat. Chem. · 2011 · 3 · 16010.1038/nchem.955 ↗
9. Zunger · 2001
10. Adv. Mater. · 2012 · 24 · 362210.1002/adma.201200732 ↗
11. RSC Adv. · 2014 · 4 · 2871410.1039/c4ra02595d ↗
12. Appl. Phys. Lett. · 2011 · 99 · 06190210.1063/1.3617458 ↗
13. Chem. Phys. Lett. · 2012 · 537 · 6210.1016/j.cplett.2012.04.025 ↗
14. Chem. Commun. · 2012 · 48 · 381810.1039/c2cc30318c ↗
15. Mater. Res. Bull. · 2008 · 43 · 199610.1016/j.materresbull.2007.10.004 ↗
16. Phys. Rev. B · 2003 · 68 · 12521010.1103/PhysRevB.68.125210 ↗
17. Phys. Rev. B · 2012 · 86 · 08532310.1103/PhysRevB.86.085323 ↗
18. J. Appl. Phys. · 2014 · 115 · 16370510.1063/1.4872250 ↗
19. Appl. Phys. Lett. · 2012 · 100 · 04210810.1063/1.3678044 ↗
20. Phys. Rev. B · 1994 · 50 · 1795310.1103/PhysRevB.50.17953 ↗
21. Phys. Rev. B · 1993 · 47 · 55810.1103/PhysRevB.47.558 ↗
22. Phys. Rev. B · 1994 · 49 · 1425110.1103/PhysRevB.49.14251 ↗
23. Comput. Mater. Sci. · 1996 · 6 · 1510.1016/0927-0256(96)00008-0 ↗
24. Comput. Phys. Commun. · 2006 · 175 · 6710.1016/j.cpc.2006.03.007 ↗
25. Adv. Mater. · 2014 · 26 · 384810.1002/adma.201400058 ↗
26. Phys. Rev. B · 2001 · 63 · 16521210.1103/PhysRevB.63.165212 ↗
27. Cryst. Res. Technol. · 2000 · 35 · 113510.1002/1521-4079(200010)35:10<1135::AID-CRAT1135>3.0.CO;2-6 ↗
28. J. Alloys Compd. · 2006 · 414 · 2610.1016/j.jallcom.2005.07.014 ↗
29. Mater. Chem. Phys. · 2014 · 147 · 43910.1016/j.matchemphys.2014.05.012 ↗
30. Phys. Rev. · 1963 · 132 · 246110.1103/PhysRev.132.2461 ↗
31. Phys. Rev. B · 2011 · 83 · 11511010.1103/PhysRevB.83.115110 ↗
32. Phys. Rev. · 1950 · 80 · 7210.1103/PhysRev.80.72 ↗
33. Appl. Phys. Lett. · 2012 · 100 · 23190310.1063/1.4726109 ↗