Low-temperature self-limiting atomic layer deposition of wurtzite InN on Si(100)
Source abstract
Abstract
In this work, we report on self-limiting growth of InN thin films at substrate temperatures as low as 200 °C by hollow-cathode plasma-assisted atomic layer deposition (HCPA-ALD). The precursors used in growth experiments were trimethylindium (TMI) and N2 plasma. Process parameters including TMI pulse time, N2 plasma exposure time, purge time, and deposition temperature have been optimized for self-limiting growth of InN with in ALD window. With the increase in exposure time of N2 plasma from 40 s to 100 s at 200 °C, growth rate showed a significant decrease from 1.60 to 0.64 Å/cycle. At 200 °C, growth rate saturated as 0.64 Å/cycle for TMI dose starting from 0.07 s. Structural, optical, and morphological characterization of InN were carried out in detail. X-ray diffraction measurements revealed the hexagonal wurtzite crystalline structure of the grown InN films. Refractive index of the InN film deposited at 200 °C was found to be 2.66 at 650 nm. 48 nm-thick InN films exhibited relatively smooth surfaces with Rms surface roughness values of 0.98 nm, while the film density was extracted as 6.30 g/cm3. X-ray photoelectron spectroscopy (XPS) measurements depicted the peaks of indium, nitrogen, carbon, and oxygen on the film surface and quantitative information revealed that films are nearly stoichiometric with rather low impurity content. In3d and N1s high-resolution scans confirmed the presence of InN with peaks located at 443.5 and 396.8 eV, respectively. Transmission electron microscopy (TEM) and selected area electron diffraction (SAED) further confirmed the polycrystalline structure of InN thin films and elemental mapping revealed uniform distribution of indium and nitrogen along the scanned area of the InN film. Spectral absorption measurements exhibited an optical band edge around 1.9 eV. Our findings demonstrate that HCPA-ALD might be a promising technique to grow crystalline wurtzite InN thin films at low substrate temperatures.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: GaN-based semiconductor devices and materials · Ga2O3 and related materials · Semiconductor Quantum Structures and Devices
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Bilkent University 1 National Nanotechnology Research Center (UNAM), , Bilkent, Ankara 06800 Turkey
Bilkent University 2 Institute of Materials Science and Nanotechnology, , Bilkent, Ankara 06800 Turkey
Funding
Tubitak, Turkey
References (42)
Show source-provided references
1. J. Appl. Phys · 2003 · 94 · 277910.1063/1.1595135 ↗
2. J. Appl. Phys. · 1999 · 85 · 91610.1063/1.369211 ↗
3. Superlattices Microstruct. · 2005 · 38 · 110.1016/j.spmi.2005.03.004 ↗
4. Phys. Status Solidi B · 2002 · 230 · R410.1002/1521-3951(200204)230:2<R4::AID-PSSB99994>3.0.CO;2-Z ↗
5. Phys. Status Solidi B · 2002 · 234 · 78710.1002/1521-3951(200212)234:3<787::AID-PSSB787>3.0.CO;2-H ↗
6. J. Vac. Sci. Technol. B · 1992 · 10 · 123710.1116/1.585897 ↗
7. J. Phys. D. Appl. Phys. · 1998 · 31 · 265310.1088/0022-3727/31/20/001 ↗
8. J. Appl. Phys · 2015 · 117 · 08431410.1063/1.4913626 ↗
9. Jpn. J. Appl. Phys. · 2013 · 5210.7567/JJAP.52.08JD06 ↗
10. Phys. Status Solidi C. · 2014 · 11 · 57710.1002/pssc.201300693 ↗
11. J. Appl. Phys. · 2013 · 114 · 16351910.1063/1.4827396 ↗
12. Semicond. Sci. Technol · 2014 · 29 · 09501010.1088/0268-1242/29/9/095010 ↗
13. Japanese J. Appl. Physics · 2003 · 42 · 254910.1143/JJAP.42.2549 ↗
14. J. Cryst. Growth · 2004 · 272 · 40010.1016/j.jcrysgro.2004.08.057 ↗
15. Phys. Status Solidi C · 2015 · 12 · 42310.1002/pssc.201400171 ↗
16. J. Vac. Sci. Technol. A · 2012 · 30 · 03151110.1116/1.4705727 ↗
17. Mater. Sci. Semicond. Process. · 2015 · 35 · 21610.1016/j.mssp.2015.02.070 ↗
18. J. Appl. Phys. · 2010 · 108 · 06353810.1063/1.3485824 ↗
19. Phys. Status Solidi · 2013 · 210 · 160610.1002/pssa.201228477 ↗
20. Thin Solid Films · 2012 · 520 · 484810.1016/j.tsf.2012.03.008 ↗
21. Phys. Status Solidi A · 2012 · 209 · 4110.1002/pssa.201100102 ↗
22. J. Vac. Sci. Technol. A · 2009 · 27 · 69610.1116/1.3151819 ↗
23. J. Mater. Chem. C · 2015 · 3 · 962010.1039/C5TC01735A ↗
24. J. Vac. Sci. Technol. A · 2016 · 34 · 01A12310.1116/1.4936072 ↗
25. Cryst. Growth Des. · 2013 · 13 · 148510.1021/cg3016172 ↗
26. J. Cryst. Growth · 2008 · 310 · 496310.1016/j.jcrysgro.2008.07.094 ↗
27. J. Vac. Sci. Technol. A · 1993 · 11 · 293110.1116/1.578670 ↗
28. J. Vac. Sci. Technol. A · 2011 · 29 · 05080110.1116/1.3609974 ↗
29. J. Appl. Phys. · 2005 · 97 · 12130110.1063/1.1940727 ↗
30. J. Mater. Chem. C · 2014 · 2 · 212310.1039/c3tc32418d ↗
31. Apl Mater. · 2014 · 2 · 09610910.1063/1.4894782 ↗
32. J. Am. Ceram. Soc · 2014 · 97 · 405210.1111/jace.13213 ↗
33. Phys. Status Solidi C · 2015 · 12 · 39410.1002/pssc.201400167 ↗
34. Jpn. J. Appl. Phys. · 1996 · 35 · 226110.1143/JJAP.35.2261 ↗
35. J. Vac. Sci. Technol. A · 1992 · 10 · 164210.1116/1.577763 ↗
36. J. Korean Phys.Soc · 2006 · 49 · 2176
37. J. Appl. Phys · 2006 · 100 · 09490210.1063/1.2363233 ↗
38. Thin Solid Films · 2008 · 516 · 501610.1016/j.tsf.2008.01.016 ↗
39. Reports Prog. Phys · 2009 · 72 · 03650210.1088/0034-4885/72/3/036502 ↗
40. J. Vac. Sci. Technol. A · 2006 · 24 · 27510.1116/1.2167970 ↗
41. Appl. Phys. A Mater. Sci. Process. · 2004 · 78 · 8910.1007/s00339-002-2002-7 ↗
42. Phys. Status Solidi B · 2002 · 229 · R110.1002/1521-3951(200202)229:3<R1::AID-PSSB99991>3.0.CO;2-O ↗