Effect of synthesis methods and a comparative study of structural and magnetic properties of zinc ferrite

Zinc ferrite samples were prepared by two different routes which are chemical co-precipitation and standard solid state double sintering method. Structural properties of ZnFe2O4 were determined, and initial particle size was found as 5 nm in the samples prepared by chemical co-precipitation technique. The XRD patterns showed the single phase of ZnFe2O4 spinel structure and confirmed by the lattice parameter and the unmixed hkl values for both the synthesis techniques. M-H curves at room temperature showed superparamagnetic nature of the samples sintered from 200°C to 600°C, synthesized by chemical co-precipitation technique. The Mössbauer analysis at room temperature showed a doublet which is the signature of superparamagnetic nature, and it is in agreement with the acquired M-H curves. The magnetization of ZnFe2O4 synthesized by chemical co-precipitation method was found higher than the magnetization of ZnFe2O4 synthesized by the solid-state double sintering method in the sintering temperature from 1100°C to 1300°C.