Ferroelectric and dielectric properties of Nd 2−x Ce x Ti 2 O 7 ceramics
Source abstract
Abstract
The solid solution system Nd2−xCexTi2O7 has been investigated. The solubility limit of Ce in Nd2−xCexTi2O7 was found to be 0·5–0·75 according to X-ray diffraction and X-ray photoelectron spectroscopy results. Ce substitution increases the b and c axes and the volume of the unit cell due to its larger ionic radius. Nd2−xCexTi2O7 (x = 0·05, 0·25, 0·5, 0·75) textured ceramics were fabricated using spark plasma sintering. The ferroelectric and dielectric properties of the ceramics were studied. Ce substitution decreases the Curie point Tc of Nd2−xCexTi2O7 compounds. The results suggest that the Tc of Ce2Ti2O7 is <1445°C.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Ferroelectric and Piezoelectric Materials · Microwave Dielectric Ceramics Synthesis · Nuclear materials and radiation effects
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (32)
Show source-provided references
1. 10.1016/0003-682X(94)90091-410.1016/0003-682X(94)90091-4 ↗
2. 10.1016/S1359-0286(98)80009-010.1016/S1359-0286(98)80009-0 ↗
3. 10.1016/j.progsolidstchem.2008.10.00110.1016/j.progsolidstchem.2008.10.001 ↗
4. 10.1016/S0079-6786(01)00002-410.1016/S0079-6786(01)00002-4 ↗
5. Ning H · J. Am. Ceram. Soc. · 2010 · 93 · 140910.1111/j.1551-2916.2009.03587.x ↗
6. 10.1111/j.1551-2916.2009.03209.x10.1111/j.1551-2916.2009.03209.x ↗
7. 10.1111/jace.1212110.1111/jace.12121 ↗
8. 10.1179/1743676112Y.000000003010.1179/1743676112Y.0000000030 ↗
9. 10.1107/S056774087500646210.1107/S0567740875006462 ↗
10. 10.1107/S056774087600826110.1107/S0567740876008261 ↗
11. 10.1107/S056774088200299410.1107/S0567740882002994 ↗
12. 10.1107/S056774088000448710.1107/S0567740880004487 ↗
13. 10.1143/JJAP.13.147310.1143/JJAP.13.1473 ↗
14. 10.1006/jssc.1994.118110.1006/jssc.1994.1181 ↗
15. Titov YA · Inorg. Mater. · 1985 · 21 · 1515
16. 10.1016/j.ssi.2009.03.01510.1016/j.ssi.2009.03.015 ↗
17. 10.1002/zaac.1992616101410.1002/zaac.19926161014 ↗
18. 10.1107/S056773947600155110.1107/S0567739476001551 ↗
19. 10.1016/0022-1902(59)80070-110.1016/0022-1902(59)80070-1 ↗
20. 10.1016/j.jeurceramsoc.2012.11.01510.1016/j.jeurceramsoc.2012.11.015 ↗
21. 10.1016/j.susc.2008.07.04010.1016/j.susc.2008.07.040 ↗
22. Szytula A · Mater. Sci. Poland · 2008 · 26 · 759
23. Lazar C · J. Optoelectron. Adv. Mater. · 2008 · 10 · 780
24. Klauda M · Physica C · 1991 · 173 · 710.1016/0921-4534(91)90801-5 ↗
25. 10.1088/0953-8984/21/48/48600410.1088/0953-8984/21/48/486004 ↗
26. 10.1002/sia.268610.1002/sia.2686 ↗
27. 10.1063/1.142625110.1063/1.1426251 ↗
28. Atuchin V. · J. Phys. D · 2009 · 42 · 610.1088/0022-3727/42/3/035305 ↗
29. 10.1063/1.32772210.1063/1.327722 ↗
30. 10.1016/0272-8842(82)90001-310.1016/0272-8842(82)90001-3 ↗
31. 10.1063/1.345989110.1063/1.3459891 ↗
32. Stevenson J · J. Electrochem. Soc. · 1996 · 143 · 272310.1149/1.1837098 ↗