Passivation‐Induced Species Dynamics and Microstructural Evolution in Solid‐State Lithium–Sulfur Cathodes

ABSTRACT Solid‐state lithium–sulfur (SSLS) batteries offer high theoretical energy density, yet their practical viability is hindered by poor sulfur utilization and limited rechargeability. At the core of this challenge lies the passivating nature of Li ₂ S, which restricts ionic and electronic transport, suppresses interfacial activity, and severely impedes the reversibility of electrochemical reactions. In this study, we elucidate the mechanistic origins of these limitations by resolving how charge and discharge species form, grow, and spatially evolve within the cathode microstructure under varied current densities and electrode compositions. By resolving the species distribution at the particle scale and coupling it with Raman spectroscopy and X‐ray diffraction, we demonstrate how Li ₂ S formation induces localized surface passivation that progressively limits electrochemical accessibility within the cathode microstructure. Sulfur utilization is found to be strongly governed by the interplay between sulfur loading, residual porosity, and interfacial architecture. High sulfur contents result in buried, electrochemically isolated domains due to poor solid electrolyte (SE) percolation, while low sulfur contents trigger SE degradation via parasitic reactions. The resulting sulfur‐porosity maps delineate the mechanistic boundaries between reversible and transport‐limited regimes, offering actionable design guidance for SSLS cathodes with enhanced sulfur utilization.