Dielectric Coating‐Induced Absorption Enhancement in Si Nanowire Junctions

Amit Solanki, Pascal Gentile, Salim Boutami, Vincent Calvo, Nicolas Pauc

Advanced Optical Materials· Volume 3· Issue 1
Publisher page

Abstract

The efficient photon management in nanowires coupled with tunable absorption can provide a significant advancement in the current solar cell technology. Adding a shell on the nanowire (NW) offers an extra degree of freedom for tailoring the NW absorption. Calculations are performed to study the shell‐induced changes in the core absorption of an ideal Si nanocylinder after enclosing it with conformal dielectrics of different thicknesses and permittivities. The calculation shows that coating the Si nanowires with nonabsorbing or weakly absorbing dielectric shells can significantly improve the mean spectral absorption efficiency of the Si core for optimized thickness and extinction. Experimental data are brought from a neighboring system consisting of individual NW junctions sandwiched between an oxidized planar Si substrate and a top‐deposited oxide layer. The measured absorption spectra show a good agreement with the theoretical spectra, with a mean spectral absorption enhancement after oxide coating as high as 5.7 in axial junctions, exceeding its theoretical counterpart that is limited to ≈1.5. Coating the nanowires with an optimized oxide shell provides a new approach to significantly enhance the light harvesting in nanowires and will lead to more efficient photovoltaics.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Nanowire Synthesis and Applications · Silicon Nanostructures and Photoluminescence · Semiconductor materials and interfaces

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

University of Grenoble Alpes INAC‐SP2M F‐38000 Grenoble France

CEA, INAC‐SP2M, SiNaPS F‐38000 Grenoble France

CEA, LETI, MINATEC Campus 17 Rue des Martyrs Grenoble 38054 France

References (30)

Show source-provided references
1. 10.1021/nl204577710.1021/nl2045777 ↗
2. 10.1016/j.mser.2010.06.01810.1016/j.mser.2010.06.018 ↗
3. 10.1073/pnas.112041510910.1073/pnas.1120415109 ↗
4. 10.1063/1.361529710.1063/1.3615297 ↗
5. 10.1021/nl100161z10.1021/nl100161z ↗
6. 10.1021/nl101379410.1021/nl1013794 ↗
7. 10.1021/nl903662710.1021/nl9036627 ↗
8. 10.1088/0957-4484/21/44/44530310.1088/0957-4484/21/44/445303 ↗
9. 10.1063/1.282111310.1063/1.2821113 ↗
10. 10.1021/nl802886y10.1021/nl802886y ↗
11. 10.1038/nature0618110.1038/nature06181 ↗
12. 10.1021/ja803290710.1021/ja8032907 ↗
13. 10.1021/nl072622p10.1021/nl072622p ↗
14. 10.1038/nmat247710.1038/nmat2477 ↗
15. 10.1016/j.nanoen.2012.05.01010.1016/j.nanoen.2012.05.010 ↗
16. 10.1021/nl301435r10.1021/nl301435r ↗
17. 10.1109/LED.2010.208642810.1109/LED.2010.2086428 ↗
18. Bohren C. F. · 2008
19. 10.1021/nl903727810.1021/nl9037278 ↗
20. 10.1364/JOSA.51.00050610.1364/JOSA.51.000506 ↗
21. For a better light power density estimate in the region of the nanowire use of a size‐calibrated pinhole placed at the focal plane of the microscope objective and in front of the photodiode can be done. However in practice the wire geometrical cross section is still smaller than the pinhole size and the power profile has still significant fluctuations in the pinhole area.
22. 10.1021/nl903166t10.1021/nl903166t ↗
23. 10.1021/nl900739a10.1021/nl900739a ↗
24. 10.1063/1.302135910.1063/1.3021359 ↗
25. 10.1016/j.physe.2008.08.05410.1016/j.physe.2008.08.054 ↗
26. 10.1021/nl201179n10.1021/nl201179n ↗
27. 10.1021/nl801952a10.1021/nl801952a ↗
28. 10.1021/nl073356i10.1021/nl073356i ↗
29. 10.1021/nl904081g10.1021/nl904081g ↗
30. 10.1088/0957-4484/23/21/21570210.1088/0957-4484/23/21/215702 ↗