Electrically Conductive Photoluminescent Porphyrin Phosphonate Metal–Organic Frameworks

Abstract Herein, the design and synthesis of a highly photoluminescent and electrically conductive metal–organic framework [Zn{Cu‐p‐H₆TPPA}]⋅2 [(CH₃)₂NH] (designated as GTUB3), which is constructed using the 5,10,15,20‐tetrakis [p‐phenylphosphonic acid] porphyrin (p‐H₈TPPA) organic linker, is reported. The bandgap of GTUB3 is measured to be 1.45 and 1.48 eV using diffuse reflectance spectroscopy and photoluminescence (PL) spectroscopy, respectively. The PL decay measurement yields a charge carrier lifetime of 40.6 ns. Impedance and DC measurements yield average electrical conductivities of 0.03 and 4 S m⁻¹, respectively, making GTUB3 a rare example of an electrically conductive 3D metal–organic framework. Thermogravimetric analysis reveals that the organic components of GTUB3 are stable up to 400 °C. Finally, its specific surface area and pore volume are calculated to be 622 m² g⁻¹ and 0.43 cm³ g⁻¹, respectively, using grand canonical Monte Carlo. Owing to its porosity and high electrical conductivity, GTUB3 may be used as a low‐cost electrode material in next generation of supercapacitors, while its low bandgap and high photoluminescence make it a promising material for optoelectronic applications.