Template‐Assisted Synthesis of Metallic 1T′‐Sn_0.3W_0.7S₂ Nanosheets for Hydrogen Evolution Reaction

Abstract Crystal phase control still remains a challenge for the precise synthesis of 2D layered metal dichalcogenide (LMD) materials. The T′ phase structure has profound influences on enhancing electrical conductivity, increasing active sites, and improving intrinsic catalytic activity, which are urgently needed for enhancing hydrogen evolution reaction (HER) activity. Theoretical calculations suggest that metastable T′ phase 2D Sn_1−xW_xS₂ alloys can be formed by combining W with 1T tin disulfide (SnS₂) as a template to achieve a semiconductor‐to‐metallic transition. Herein, 2D Sn_1−xW_xS₂ alloys with varying x are prepared by adjusting the molar ratio of reactants via hydrothermal synthesis, among which Sn_0.3W_0.7S₂ displays a maximum of concentration of 81% in the metallic phase and features a distorted octahedral‐coordinated metastable 1T′ phase structure. The obtained 1T′‐Sn_0.3W_0.7S₂ has high intrinsic electrical conductivity, lattice distortion, and defects, showing a prominently improved HER catalytic performance. Metallic Sn_0.3W_0.7S₂ coupled with carbon black exhibits at least a 215‐fold improvement compared to pristine SnS₂. It has excellent long‐term durability and HER activity. This work reveals a general phase transition strategy by using T phase materials as templates and merging heteroatoms to achieve synthetic metastable phase 2D LMDs that have a significantly improved HER catalytic performance.