Enhancing Stability of Efficient Perovskite Solar Cells (PCE ≈ 24.5%) by Suppressing PbI₂ Inclusion Formation

Abstract Excess lead(II) iodide (PbI₂) has controversial roles in affecting the efficiency of perovskite solar cells (PSCs). Since the photoinstability of PbI₂ is now known to largely accelerate perovskite degradation, suppressing and/or eliminating excess PbI₂ is key to improving the stability of PSCs. Herein, process‐dependent PbI₂ formation on the surfaces of formamidinium lead triiodide (FAPbI₃) films is examined. Due to the faster evaporation rate of organic substances, crystalline PbI₂ as an inclusion is found within the triple junction grain boundaries. With this hypothesis, two strategies are suggested: control of the 1) vapor pressure and 2) stoichiometry of precursor solutions to induce sufficient reaction of FAPbI₃. Although both strategies successfully eliminate the PbI₂ as inclusions, due to the slower evaporation rate, vapor pressure control films also exhibit a larger grain size (≈1.18 µm) with a good film quality to attain the highest power conversion efficiency (PCE) of 24.5%. Furthermore, the phase stability of α‐FAPbI₃ is improved due to the elimination of the degradation sites induced by the photoinstability of PbI₂. The findings explore the formation process of unwanted PbI₂ (≈2.8%) and provide a simple method to effectively suppress its formation. This may further boost the PCE and stability, especially for FA‐based perovskites.