3D Polydentate Complexing Agents for Passivating Defects and Modulating Crystallinity for High‐Performance Perovskite Solar Cells

Abstract The grain boundaries (GBs)/surface defects within perovskite film directly impede the further improvement of photoelectric conversion efficiency (PCE) and stability of planar perovskite solar cells (PSCs). Herein, 3D phytic acid (PA) and phytic acid dipotassium (PAD) with polydentate are explored to synchronously passivate the defects of perovskite absorber directly in multiple spatial directions. The strong electron‐donating groups (H₂PO₄) in the PA molecule afford six anchor sites to bind firmly with uncoordinated Pb²⁺ at the GBs/surface and modulate perovskite crystallization, thus enhancing the quality of perovskite film. Particularly, PAD containing an additional (K→PO) push–pull structure promotes the dominant coordination of phosphate group (PO) with Pb²⁺ and passivates halide anion defects due to the complexation of potassium ions (K⁺) with iodide ions (I^‐). Consequently, the PAD‐complexed PSCs deliver a champion PCE of 23.18%, which is remarkably higher than that of the control device (19.94%). Meanwhile, PAD‐complexed PSCs exhibit superior moisture and thermal stability, remaining 79% of their initial PCE after 1000 h under continuous illumination, while the control device remain only 48% of their PCE after 1000 h. This work provides important insights into designing multifunctional 3D passivators for the purpose of simultaneously enhancing the efficiency and stability of devices.