Structural Diversity, Thermal, and Semiconducting Characteristics of Two N,N′-bis(phosphonomethyl)-1,4,5,8-Naphthalenediimide-Based Compounds

Two crystals of N,N′-bis(phosphonomethyl)-1,4,5,8-naphthalenediimide were grown in the presence of neutral (water) and charged (imidazolium cation) species, yielding [(H2O3P)CH2-(C14H4N2O4)-CH2(PO3H2)]∙H2O (1) and [C3H5N2][(H1.5O3P)CH2-(C14H4N2O4)-CH2(PO3H1.5)] (2), respectively. The ligand N,N′-bis(phosphonomethyl)-1,4,5,8-naphthalenediimide was synthesized via the condensation of naphthalene-1,4,5,8-tetracarboxylic dianhydride with (aminomethyl)phosphonic acid in N,N′-dimethylformamide or imidazole. The flexible N-methyl phosphonic acid groups adopt a cis configuration in compound 1 and a trans configuration in compound 2. In compound 1, the phosphonate groups engage in extensive hydrogen bonding, as well as with water molecules and π–π stacking, resulting in a three-dimensional closely packed structure. Compound 2 forms a densely packed three-dimensional network stabilized by charge-assisted hydrogen bonding (anion-cation), anion–π interactions, and π–π stacking interactions. Hirshfeld surface analysis was conducted and the associated two-dimensional fingerprint plots were generated to further elucidate the nature and contributions of these noncovalent interactions. Direct bandgap measurements estimated from Tauc plots yielded values of 2.92 eV and 2.85 eV for compounds 1 and 2, respectively, highlighting their potential as promising n-type organic semiconductors. Thermal analysis reveals that compound 2 exhibits greater thermal stability than compound 1.