Strategies for Enhanced Optical Performance and Durability of VO2‐Based Thermochromic Windows
Source abstract
Abstract
Due to the growing need for smart windows for buildings to reduce energy usage, vanadium dioxide (VO2) has been investigated as a potential material for thermochromic smart windows due to its ease of implementation and simplicity in industrial production. VO2 undergoes a reversible phase shift from a monoclinic (M, P21/c) semiconductor to a rutile (R, P42/mnm) metal at a critical temperature of 68 °C. This transition is accompanied by acute variations in IR reflectance, transmittance, and electrical resistance. Despite substantial developments in thermochromic materials, their optical and transition properties are still unsatisfactory. In the past several decades, many methods for enhancing optical properties have been reported, including composite films, multilayer structures, and element doping. Recent developments in thermochromic smart windows to improve both optical properties and durability have been surveyed in this review. Additionally, future growth trends have been provided by the possibility of commercially manufacturing VO2 smart windows.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Transition Metal Oxide Nanomaterials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Graduate School of Nanoscience and Technology Chulalongkorn University 10330 Bangkok Thailand
Department of Physics Faculty of Science Chulalongkorn University 10330 Bangkok Thailand
Funding
Office of the Permanent Secretary, Ministry of Higher Education, Science, Research and Innovation, Thailand
References (100+)
Show source-provided references
1. 10.1016/j.enbuild.2017.10.06910.1016/j.enbuild.2017.10.069 ↗
2. 10.1016/j.solmat.2009.08.02110.1016/j.solmat.2009.08.021 ↗
3. 10.1002/adfm.20180011310.1002/adfm.201800113 ↗
4. 10.1016/j.rser.2007.05.00110.1016/j.rser.2007.05.001 ↗
5. 2018
6. 10.1039/c1ee02092g10.1039/c1ee02092g ↗
7. 10.1016/S0927-0248(99)00088-410.1016/S0927-0248(99)00088-4 ↗
8. 10.1016/j.joule.2018.06.01810.1016/j.joule.2018.06.018 ↗
9. 10.1016/j.mtener.2021.10082710.1016/j.mtener.2021.100827 ↗
10. 10.1002/adom.20130003410.1002/adom.201300034 ↗
11. 10.1364/OL.30.00055810.1364/OL.30.000558 ↗
12. 10.1016/j.enbuild.2021.11102210.1016/j.enbuild.2021.111022 ↗
13. 10.1115/1.402476810.1115/1.4024768 ↗
14. 10.1002/aenm.20160220910.1002/aenm.201602209 ↗
15. 10.1016/j.joule.2018.12.01010.1016/j.joule.2018.12.010 ↗
16. 10.1016/0165-1633(87)90029-310.1016/0165-1633(87)90029-3 ↗
17. 10.1016/j.solmat.2013.03.04310.1016/j.solmat.2013.03.043 ↗
18. 10.1103/PhysRevLett.3.3410.1103/PhysRevLett.3.34 ↗
19. 10.1016/j.solmat.2013.05.06110.1016/j.solmat.2013.05.061 ↗
20. 10.1016/j.apenergy.2022.11905310.1016/j.apenergy.2022.119053 ↗
21. 10.1039/C4TA05035E10.1039/C4TA05035E ↗
22. 10.1016/j.enbuild.2010.04.01010.1016/j.enbuild.2010.04.010 ↗
23. 10.1021/acs.chemrev.2c0076210.1021/acs.chemrev.2c00762 ↗
24. 10.3389/fenrg.2021.80038210.3389/fenrg.2021.800382 ↗
25. 10.3390/nano1110267410.3390/nano11102674 ↗
26. 10.3390/nano1101023910.3390/nano11010239 ↗
27. American Society for Testing and Materials Committee G03 on Weathering and Durability2003.
28. 10.1039/D2NR01864K10.1039/D2NR01864K ↗
29. 10.1021/acsanm.2c0013810.1021/acsanm.2c00138 ↗
30. 10.1016/j.ceramint.2019.09.26410.1016/j.ceramint.2019.09.264 ↗
31. 10.1126/sciadv.aav681510.1126/sciadv.aav6815 ↗
32. 10.1016/j.matchemphys.2019.12223010.1016/j.matchemphys.2019.122230 ↗
33. 10.1016/j.jssc.2013.10.04010.1016/j.jssc.2013.10.040 ↗
34. 10.1039/D0TC02785E10.1039/D0TC02785E ↗
35. 10.1016/j.jallcom.2020.15632310.1016/j.jallcom.2020.156323 ↗
36. 10.1016/j.apsusc.2023.15760710.1016/j.apsusc.2023.157607 ↗
37. 10.1016/j.vacuum.2020.10935210.1016/j.vacuum.2020.109352 ↗
38. 10.1007/s10971-019-04999-010.1007/s10971-019-04999-0 ↗
39. 10.1016/j.solmat.2023.11231110.1016/j.solmat.2023.112311 ↗
40. 10.1016/j.matlet.2021.13008610.1016/j.matlet.2021.130086 ↗
41. 10.1016/j.tsf.2011.08.03510.1016/j.tsf.2011.08.035 ↗
42. 10.1016/j.matdes.2019.10839610.1016/j.matdes.2019.108396 ↗
43. 10.1016/j.jssc.2022.12311710.1016/j.jssc.2022.123117 ↗
44. 10.1016/j.solmat.2016.08.03510.1016/j.solmat.2016.08.035 ↗
45. 10.1016/j.supflu.2020.10498910.1016/j.supflu.2020.104989 ↗
46. 10.1039/C6RA16667A10.1039/C6RA16667A ↗
47. 10.1063/1.348798010.1063/1.3487980 ↗
48. 10.1039/C8TC00859K10.1039/C8TC00859K ↗
49. 10.1016/j.jallcom.2021.15988810.1016/j.jallcom.2021.159888 ↗
50. 10.1002/admi.20160016410.1002/admi.201600164 ↗
51. 10.1016/j.ceramint.2018.11.03610.1016/j.ceramint.2018.11.036 ↗
52. 10.1103/PhysRevLett.93.17740310.1103/PhysRevLett.93.177403 ↗
53. 10.1021/cm703330710.1021/cm7033307 ↗
54. 10.1039/c3ta14822j10.1039/c3ta14822j ↗
55. 10.1016/j.jcis.2013.11.02810.1016/j.jcis.2013.11.028 ↗
56. 10.1016/j.solmat.2007.06.01610.1016/j.solmat.2007.06.016 ↗
57. 10.1039/C8NA00238J10.1039/C8NA00238J ↗
58. 10.1016/j.solener.2014.06.02510.1016/j.solener.2014.06.025 ↗
59. 10.1016/j.matpr.2015.08.03010.1016/j.matpr.2015.08.030 ↗
60. 10.1021/la404666n10.1021/la404666n ↗
61. 10.1038/s41598-022-15439-510.1038/s41598-022-15439-5 ↗
62. 10.1039/c3ta12232h10.1039/c3ta12232h ↗
63. 10.1039/c3ta14612j10.1039/c3ta14612j ↗
64. Li B. · Adv. Opt. Mater. · 2023 · 2302042
65. 10.1016/j.ceramint.2022.09.19910.1016/j.ceramint.2022.09.199 ↗
66. 10.1016/j.solmat.2009.03.02110.1016/j.solmat.2009.03.021 ↗
67. 10.1021/cm034905y10.1021/cm034905y ↗
68. Livage J. · J. Solgel. Sci. Technol. · 1998 · 7 · 915
69. 10.1021/co500064p10.1021/co500064p ↗
70. 10.1149/06102.0387ecst10.1149/06102.0387ecst ↗
71. Kittiwatanakul S. · Proc. SPIE · 2018 · 10656 · 106560A
72. 10.1143/JJAP.50.01BE0410.1143/JJAP.50.01BE04 ↗
73. 10.1016/S0040-6090(01)01603-010.1016/S0040-6090(01)01603-0 ↗
74. 10.1039/c3cp50638j10.1039/c3cp50638j ↗
75. 10.1063/1.10238810.1063/1.102388 ↗
76. 10.1016/j.tsf.2011.01.40110.1016/j.tsf.2011.01.401 ↗
77. 10.1063/1.491943310.1063/1.4919433 ↗
78. 10.1016/j.ceramint.2013.10.08310.1016/j.ceramint.2013.10.083 ↗
79. 10.1039/c3cp52009a10.1039/c3cp52009a ↗
80. 10.1063/1.486293010.1063/1.4862930 ↗
81. 10.1016/j.solmat.2020.11044310.1016/j.solmat.2020.110443 ↗
82. 10.1016/j.solmat.2011.01.00910.1016/j.solmat.2011.01.009 ↗
83. 10.35848/1347-4065/ac103810.35848/1347-4065/ac1038 ↗
84. 10.1016/j.apsusc.2021.15095910.1016/j.apsusc.2021.150959 ↗
85. 10.1016/j.solmat.2012.11.01110.1016/j.solmat.2012.11.011 ↗
86. 10.4028/www.scientific.net/AMR.284-286.217710.4028/www.scientific.net/AMR.284-286.2177 ↗
87. 10.3390/ma1601046110.3390/ma16010461 ↗
88. 10.1016/j.solmat.2019.04.02210.1016/j.solmat.2019.04.022 ↗
89. 10.1016/j.jallcom.2021.16035210.1016/j.jallcom.2021.160352 ↗
90. 10.1021/acsaem.0c0165110.1021/acsaem.0c01651 ↗
91. 10.1016/S0040-6090(98)01406-010.1016/S0040-6090(98)01406-0 ↗
92. 10.1143/JJAP.34.245910.1143/JJAP.34.2459 ↗
93. 10.1039/C5TC01062D10.1039/C5TC01062D ↗
94. 10.1039/C4TA02880E10.1039/C4TA02880E ↗
95. 10.1063/5.004451610.1063/5.0044516 ↗
96. 10.1166/jnn.2019.1661810.1166/jnn.2019.16618 ↗
97. 10.1016/j.ceramint.2019.10.21110.1016/j.ceramint.2019.10.211 ↗
98. 10.1039/c3cp51359a10.1039/c3cp51359a ↗
99. 10.1016/j.tsf.2011.10.05310.1016/j.tsf.2011.10.053 ↗
100. 10.1016/j.nanoen.2011.12.00210.1016/j.nanoen.2011.12.002 ↗