In Situ Grain Boundary Functionalization for Stable and Efficient Inorganic CsPbI2Br Perovskite Solar Cells
Source abstract
Abstract
Abstract The phase instability and large energy loss are two obstacles to achieve stable and efficient inorganic‐CsPbI3−xBrx perovskite solar cells. In this work, stable cubic perovskite (α)‐phase CsPbI2Br is successfully achieved by Pb(Ac)2 functioning at the grain boundary under low temperature. Ac− strongly coordinates with CsPbI2Br to stabilize the α‐phase and also make the grain size smaller and film uniform by fast nucleation. PbO is formed in situ at the grain boundary by decomposing Pb(Ac)2 at high‐temperature annealing. The semiconducting PbO effectively passivates the surface states, reduces the interface recombination, and promotes the charge transport in CsPbI2Br perovskite solar cells. A 12% efficiency and good stability are obtained for in situ PbO‐passivated CsPbI2Br solar cells, while Pb(Ac)2‐passivated device exhibits 8.7% performance and the highest stability, much better than the control device with 8.5% performance and inferior stability. This article highlights the extrinsic ionic grain boundary functionalization to achieve stable and efficient inorganic CsPbI3−xBrx materials and the devices.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Perovskite Materials and Applications · Quantum Dots Synthesis And Properties · Conducting polymers and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Microelectronic Science and Engineering Ningbo University Zhejiang 315211 China
School of Materials Science and Engineering Ningbo University of Technology Zhejiang 315016 China
Photovoltaics Materials Unit National Institute for Materials Science Tsukuba Ibaraki 305‐0047 Japan
Funding
National Natural Science Foundation of China · Natural Science Foundation of Zhejiang Province · Ningbo University
References (36)
Show source-provided references
1. 10.1002/aenm.20150047710.1002/aenm.201500477 ↗
2. 10.1039/C5TA00358J10.1039/C5TA00358J ↗
3. 10.1039/C5TA06398A10.1039/C5TA06398A ↗
4. 10.1002/aenm.20150245810.1002/aenm.201502458 ↗
5. 10.1002/adma.20170539310.1002/adma.201705393 ↗
6. 10.1021/jacs.7b1322910.1021/jacs.7b13229 ↗
7. 10.1021/acsenergylett.7b0119710.1021/acsenergylett.7b01197 ↗
8. 10.1126/science.aag270010.1126/science.aag2700 ↗
9. 10.1021/acs.nanolett.7b0210110.1021/acs.nanolett.7b02101 ↗
10. 10.1039/C6CC08282C10.1039/C6CC08282C ↗
11. 10.1021/jacs.7b0862810.1021/jacs.7b08628 ↗
12. 10.1021/acs.nanolett.6b0063510.1021/acs.nanolett.6b00635 ↗
13. 10.1021/jacs.7b0794910.1021/jacs.7b07949 ↗
14. 10.1021/jacs.7b0400010.1021/jacs.7b04000 ↗
15. 10.1039/C5TA06398A10.1039/C5TA06398A ↗
16. 10.1038/ncomms714210.1038/ncomms7142 ↗
17. 10.1021/acs.jpclett.6b0000210.1021/acs.jpclett.6b00002 ↗
18. 10.1021/acs.jpclett.7b0106710.1021/acs.jpclett.7b01067 ↗
19. 10.1021/acs.chemmater.5b0410710.1021/acs.chemmater.5b04107 ↗
20. 10.1021/acs.chemmater.7b0294810.1021/acs.chemmater.7b02948 ↗
21. 10.1021/nl504877910.1021/nl5048779 ↗
22. 10.1021/acs.nanolett.7b0150010.1021/acs.nanolett.7b01500 ↗
23. 10.1039/C5EE03255E10.1039/C5EE03255E ↗
24. 10.1021/jp036401t10.1021/jp036401t ↗
25. 10.1016/0040-6031(94)80273-410.1016/0040-6031(94)80273-4 ↗
26. 10.1021/jp310233210.1021/jp3102332 ↗
27. 10.1023/A:100664142949910.1023/A:1006641429499 ↗
28. 10.1038/s41563-017-0006-010.1038/s41563-017-0006-0 ↗
29. 10.1039/C5EE00645G10.1039/C5EE00645G ↗
30. 10.1039/C4EE00762J10.1039/C4EE00762J ↗
31. 10.1021/acs.jpclett.6b0021510.1021/acs.jpclett.6b00215 ↗
32. 10.1039/c3ee43822h10.1039/c3ee43822h ↗
33. 10.1126/science.aan230110.1126/science.aan2301 ↗
34. Wang Q. Z. · Chin. J. Chem. · 1996 · 14 · 24410.1002/cjoc.19960140310 ↗
35. 10.1039/C5EE03560K10.1039/C5EE03560K ↗
36. 10.1002/aenm.20170103810.1002/aenm.201701038 ↗