In situ growth of lead zirconate titanate thin films by hybrid process: sol–gel method and pulsed-laser deposition
Source abstract
Abstract
Pb(Zr{sub x}Ti{sub 1-x})O{sub 3} (PZT) thin films were grown in situ on Pt/Ti/SiO{sub 2}/Si substrates by a hybrid process consisting of the sol-gel method and pulsed-laser deposition (PLD). The deposition temperature to obtain the perovskite phase in the hybrid process is 460 deg C, significantly lower than in the case of direct film deposition by PLD on a Pt/Ti/SiO{sub 2}/Si substrate. X-ray diffraction analysis indicated that the preferred orientation of PZT films can be controlled using the layer deposited by the sol-gel method and highly (1 1 1)- or (1 0 0)-oriented PZT films were obtained. A transmission electron microscope image showed that the film had a polycrystalline columnar microstructure extending through its thickness, and no sharp boundary was observed between the layers deposited by the sol-gel method and PLD. A high-resolution electron microscope image and electron diffraction analysis revealed that the crystalline lattice of the layers deposited by the sol-gel method and PLD was continuous and there was no difference in crystalline orientation between the layers. These results indicate that the solid-phase epitaxial effect between the PZT layers deposited by the sol-gel method and PLD reduces the deposition temperature to obtain the perovskite phase during PLD, and causes themore » films to exhibit the same preferred orientation as that of the layer deposited by the sol-gel method. The dielectric constant and remanent polarization of the films deposited in situ at 460 deg C were approximately 900 and 15 {mu}C/cm{sup 2}, respectively.« less
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Ferroelectric and Piezoelectric Materials · Acoustic Wave Resonator Technologies · Electronic and Structural Properties of Oxides
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. Auciello · Phys Today · 1998 · 51 · 2210.1063/1.882324 ↗
2. Spearing · Acta Mater · 2000 · 48 · 17910.1016/S1359-6454(99)00294-3 ↗
3. Polla · Mater Res Soc Bull · 1996 · 21 · 5910.1557/S0883769400035934 ↗
4. Chu · Jpn J Appl Phys · 1999 · 38 · L148210.1143/JJAP.38.L1482 ↗
5. Chu · J Vac Sci Technol · 2000 · B18 · 360410.1116/1.1319684 ↗
6. Tsaur · Jpn J Appl Phys · 2002 · 41 · 666410.1143/JJAP.41.6664 ↗
7. Ramesh · Mater Sci Eng · 2001 · R32 · 19110.1016/S0927-796X(00)00032-2 ↗
8. Maeda · Jpn J Appl Phys · 1998 · 37 · 711610.1143/JJAP.37.7116 ↗
9. Wang · Proc SPIE · 1999 · 3680 · 94810.1117/12.341162 ↗
10. Wang · Thin Solid Films · 2002 · 416 · 6610.1016/S0040-6090(02)00723-X ↗
11. Horwitz · Appl Phys Lett · 1991 · 59 · 156510.1063/1.106284 ↗
12. Roy · Appl Phys Lett · 1991 · 69 · 7390
13. Verardi · Appl Surf Sci · 1996 · 96-98 · 77510.1016/0169-4332(95)00591-9 ↗
14. Zheng · J Mater Res · 1997 · 12 · 117910.1557/JMR.1997.0164 ↗
15. Wang · Jpn J Appl Phys · 2000 · 39 · 541310.1143/JJAP.39.5413 ↗
16. Wang · Jpn J Appl Phys · 2001 · 40 · 552310.1143/JJAP.40.5523 ↗
17. Wang · J Am Ceram Soc · 2002 · 85 · 310810.1111/j.1151-2916.2002.tb00592.x ↗
18. Wang · Jpn J Appl Phys · 2003 · 42 · 593610.1143/JJAP.42.5936 ↗
19. Liu · J Am Ceram Soc · 1996 · 79 · 49510.1111/j.1151-2916.1996.tb08151.x ↗
20. Liu · J Am Ceram Soc · 1997 · 80 · 241010.1111/j.1151-2916.1997.tb03134.x ↗
21. Law · Thin Solid Films · 1998 · 335 · 22010.1016/S0040-6090(98)00813-X ↗
22. Wang · J Japan Inst Metals · 2000 · 64 · 38310.2320/jinstmet1952.64.5_383 ↗
23. Wang · Jpn J Appl Phys · 2002 · 41 · 665810.1143/JJAP.41.6658 ↗
24. Wang · J Cryst Growth · 2004 · 267 · 9210.1016/j.jcrysgro.2004.03.011 ↗
25. Wang · J Cryst Growth · 2004 · 262 · 35910.1016/j.jcrysgro.2003.10.072 ↗
26. Kim · Jpn J Appl Phys · 2002 · 41 · 381710.1143/JJAP.41.3817 ↗
27. Eun · Thin Solid Films · 1999 · 357 · 23210.1016/S0040-6090(99)00643-4 ↗