Upcycling of poly(ethylene terephthalate) and a feasibility of applying poly(ethylene terephthalate) /graphene composite sheets for organic photovoltaic device encapsulation

This work has concerned upcycling of used PET bottles by compounding with graphene nanoplatelets (GNP). The effects of antioxidants concentration on molecular weight and mechanical properties of the recycled PET sheets were examined, using ¹ H-NMR spectroscopy and a universal testing machine, respectively. The optimum antioxidants concentration was found to be 1.5 phr, as it is effectively mitigated PET chain scission. When loaded with 0.2 phr of GNP, the crystallinity of the PET/GNP sheets increased from 20.11% to 25.75% while the water vapor transmission rate of the PET sheet dropped from 16.795 (g.mm/m ² .day) to 11.585 (g.mm/m ² .day) accordingly. The improvements were obtained at the expense of visible light transmittance which decreased from 77.70% to 10.76%. A similar but more pronounced effect was observed when a surface-functionalized GNP was used. For the encapsulation of organic photovoltaic (OPV) cells, PET composite sheet containing 0.025 phr of GNP was chosen. After 2 weeks, the normalized PCE of OPV cells encapsulated with recycled PET sheets were about 0.61–0.62, whereas that of the bear OPV cell dropped rapidly to 0.20. In overall, this work demonstrated a feasibility of using PET/GNP composite sheets as a cover lid for encapsulation of OPV, aiming to enhance durability and lifespan of the devices.