Optically Controlled Phase Transitions in 2D Se Allotropes
Source abstract
Abstract
Due to the advantages in high response speed and nonvolatility, materials with optically controlled phase transitions are promising candidates for data storage applications. In this work, we use real-time time-dependent density functional theory (rt-TDDFT) simulations to demonstrate that phase transitions can be precisely manipulated in two-dimensional (2D) ferroelectric α-Se through the application of an appropriate laser pulse. Unlike thermal activation, selected coherent phonon modes are activated optically. Specifically, the activations of A-1 and A-2 phonon modes at the Γ-point result in the transition to a state with an opposite electrical polarization. Through momentum scattering, these two phonon modes coherently evolve into phonon modes at the S -point. Then resultant nonequilibrium atomic dynamics, originating from the activation of three dominant B-1(S), B-2(S), and B-3(S) at S -point, facilitate the formation of a previously unexplored 2D selenium allotrope, which we refer to as r -Se.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Phase-change materials and chalcogenides · Chalcogenide Semiconductor Thin Films · Advanced Semiconductor Detectors and Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Physics
Southeast University
Key Laboratory of Quantum Materials and Devices of Ministry of Education
Beijing National Laboratory for Condensed Matter Physics and Institute of Physics
Chinese Academy of Sciences
Songshan Lake Materials Laboratory
Funding
National Key Research and Development Program of China · National Natural Science Foundation of China · Chinese Academy of Sciences
References (39)
Show source-provided references
1. 10.1103/PhysRevLett.21.145010.1103/PhysRevLett.21.1450 ↗
2. 10.1038/nmat233010.1038/nmat2330 ↗
3. 10.1038/nmat200910.1038/nmat2009 ↗
4. 10.1146/annurev-matsci-082908-14540510.1146/annurev-matsci-082908-145405 ↗
5. 10.1016/j.applthermaleng.2007.08.00910.1016/j.applthermaleng.2007.08.009 ↗
6. 10.1021/acs.chemrev.2c0040710.1021/acs.chemrev.2c00407 ↗
7. 10.1021/acs.jpclett.4c0295110.1021/acs.jpclett.4c02951 ↗
8. 10.1021/acs.chemmater.5c0015210.1021/acs.chemmater.5c00152 ↗
9. 10.1016/j.mattod.2018.03.02910.1016/j.mattod.2018.03.029 ↗
10. 10.1063/1.508786410.1063/1.5087864 ↗
11. 10.1002/smll.20180202510.1002/smll.201802025 ↗
12. 10.1038/nmat215710.1038/nmat2157 ↗
13. 10.1038/nchem.100710.1038/nchem.1007 ↗
14. 10.1038/ncomms936710.1038/ncomms9367 ↗
15. 10.1063/1.34862010.1063/1.348620 ↗
16. 10.1103/PhysRevB.82.04120310.1103/PhysRevB.82.041203 ↗
17. 10.1103/PhysRevMaterials.6.10340310.1103/PhysRevMaterials.6.103403 ↗
18. 10.1063/1.32343910.1063/1.323439 ↗
19. 10.1143/JPSJS.76SA.1710.1143/JPSJS.76SA.17 ↗
20. 10.1103/PhysRevB.98.03542010.1103/PhysRevB.98.035420 ↗
21. 10.1021/acsnano.0c0312410.1021/acsnano.0c03124 ↗
22. 10.1103/PhysRevB.13.138310.1103/PhysRevB.13.1383 ↗
23. 10.1021/acsnano.7b0478610.1021/acsnano.7b04786 ↗
24. 10.1021/acs.nanolett.1c0229410.1021/acs.nanolett.1c02294 ↗
25. 10.1038/007303e010.1038/007303e0 ↗
26. 10.1098/rspl.1876.002410.1098/rspl.1876.0024 ↗
27. 10.2475/ajs.s3-26.156.46510.2475/ajs.s3-26.156.465 ↗
28. 10.1063/1.296062810.1063/1.2960628 ↗
29. 10.1063/1.503654310.1063/1.5036543 ↗
30. 10.1002/adts.20180005510.1002/adts.201800055 ↗
31. 10.1103/PhysRevLett.52.99710.1103/PhysRevLett.52.997 ↗
32. 10.1103/PhysRevB.62.799810.1103/PhysRevB.62.7998 ↗
33. 10.1103/PhysRevLett.114.06300410.1103/PhysRevLett.114.063004 ↗
34. 10.1002/wcms.149210.1002/wcms.1492 ↗
35. 10.1103/PhysRevB.43.199310.1103/PhysRevB.43.1993 ↗
36. 10.1088/0953-8984/20/6/06420810.1088/0953-8984/20/6/064208 ↗
37. 10.6028/jres.049.04410.6028/jres.049.044 ↗
38. 10.1088/1361-648X/acd83110.1088/1361-648X/acd831 ↗
39. 10.7566/JPSJ.92.01200110.7566/JPSJ.92.012001 ↗