Drastic improvement of oxide thermoelectric performance using thermal and plasma treatments of the InGaZnO thin films grown by sputtering
Source abstract
Abstract
Abstract Single-crystal InGaO 3 (ZnO) m thin films with periodic superlattice structures suitable for transparent thermoelectric applications were fabricated using a commercially available c -plane sapphire substrate, an epitaxial ZnO buffer layer, a thermal treatment at 900 °C, and an Ar plasma treatment. The introduction of the epitaxial ZnO buffer layer led to a significant reduction in the lattice mismatch at the interface with the InGaO 3 (ZnO) m films. The sandwich structure of the ZnO/InGaZnO/ZnO resulted in an increase in the ZnO content in the superlattice InGaO 3 (ZnO) m thin films. With respect to thermoelectric properties, the formation of a perfect, layered structure induced an increase in the Seebeck coefficient and, at the same time, a decrease in the thermal conductivity. After complete crystallization, the Ar plasma treatment resulted in a considerable decrease in the electrical resistivity without microstructural changes and without a large decrease in the thermal conductivity. As a result, the thermoelectric properties using n -type oxide semiconductors were dramatically improved.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced Thermoelectric Materials and Devices · ZnO doping and properties · Chalcogenide Semiconductor Thin Films
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (35)
Show source-provided references
1. Vining · Nat Mater · 2009 · 8 · 8310.1038/nmat2361 ↗
2. Kanatzidis · 2002
3. Snyder · Nat Mater · 2008 · 7 · 10510.1038/nmat2090 ↗
4. Böttner · MRS Bull · 2006 · 31 · 21110.1557/mrs2006.47 ↗
5. Urban · Nat Mater · 2007 · 6 · 11510.1038/nmat1826 ↗
6. Boukai · Nature · 2008 · 451 · 16810.1038/nature06458 ↗
7. Dresselhaus · Adv Mater · 2007 · 19 · 104310.1002/adma.200600527 ↗
8. Venkatasubramanian · Nature · 2001 · 413 · 59710.1038/35098012 ↗
9. Xiaofang · J Phys D: Appl Phys · 2009 · 42 · 22530310.1088/0022-3727/42/22/225303 ↗
10. Obara · Jpn J Appl Phys · 2004 · 43 · L54010.1143/JJAP.43.L540 ↗
11. Sugiura · Appl Phys Lett · 2006 · 89 · 03211110.1063/1.2234277 ↗
12. Strobel · J. Solid State Chem · 2009 · 182 · 187210.1016/j.jssc.2009.04.030 ↗
13. Jalan · Appl Phys Lett · 2010 · 97 · 04210610.1063/1.3471398 ↗
14. Nomura · Appl Phys Lett · 2004 · 95 · 199310.1063/1.1788897 ↗
15. Lee · IEEE Electron Dev Lett · 2010 · 31 · 22510.1109/LED.2009.2038806 ↗
16. Kim · Appl Phys Lett · 2007 · 90 · 21211410.1063/1.2742790 ↗
17. Ohta · Adv Funct Mater · 2003 · 13 · 13910.1002/adfm.200390020 ↗
18. Seo · Cryst Growth Des · 2010 · 10 · 463810.1021/cg100924a ↗
19. Baxter · J Cryst Growth · 2005 · 274 · 40710.1016/j.jcrysgro.2004.10.014 ↗
20. Ravila · J Cryst Growth · 1991 · 114 · 56910.1016/0022-0248(91)90402-Q ↗
21. Chen · J Appl Phys · 1998 · 84 · 391210.1063/1.368595 ↗
22. Nomura · J Appl Phys · 2004 · 95 · 553210.1063/1.1712010 ↗
23. Girtan · Surf Coat Technol · 2003 · 172 · 24210.1016/S0257-8972(03)00334-7 ↗
24. Chen · J Phys Chem C · 2008 · 112 · 2039310.1021/jp808194r ↗
25. Ohta · Phys Stat Sol (b) · 2008 · 245 · 236210.1002/pssb.200844248 ↗
26. Martin · Phys Rev B · 2009 · 79 · 11531110.1103/PhysRevB.79.115311 ↗
27. Zide · Phys Rev B · 2006 · 74 · 20533510.1103/PhysRevB.74.205335 ↗
28. Hicks · Phys Rev B · 1993 · 47 · 1272710.1103/PhysRevB.47.12727 ↗
29. Ahn · Appl Phys Lett · 2008 · 93 · 20350610.1063/1.3028340 ↗
30. Park · Appl Phys Lett · 2007 · 90 · 26210610.1063/1.2753107 ↗
31. Cahill · Rev Sci Instrum · 1990 · 61 · 80210.1063/1.1141498 ↗
32. Takashiri · J Appl Phys · 2007 · 101 · 07430110.1063/1.2717867 ↗
33. Kim · Int J Thermophysics · 2004 · 25 · 28110.1023/B:IJOT.0000022340.65615.22 ↗
34. Wojciechowski · J Achiev Mater Manuf Eng · 2009 · 37 · 512
35. Datta · Cryst Growth Des · 2010 · 10 · 398310.1021/cg100560s ↗