La-Based Perovskite Oxide Catalysts for Alkaline Oxygen Reduction: The Importance of Electrochemical Stability

Alkaline fuel cells represent a promising energy conversion technology since they enable the use of precious metal-free electrocatalysts for the oxygen reduction reaction. Among these, La-based perovskite oxides, with great compositional and structural tunability, are especially attractive. However, we believe that the current literature lacks a thorough understanding of their inherent (in)stability issues. Here, we report on nine La-based perovskite oxide electrocatalysts for the oxygen reduction reaction, including LaMO 3 (M = Mn, Co, Ni) and LaCo x M 1– x O 3 (M = Mn, Ni; x = 0.9, 0.5, 0.1). While some exhibited initial promising activity, they all degraded significantly, even after brief electrochemical testing. Through comprehensive structural characterization of LaCo 0.9 Mn 0.1 O 3, particularly scanning transmission electron microscopy, we found evidence to support a degradation mechanism in which the B-site cation species irreversibly leach from the perovskite under testing conditions. A sample cycled 10 000 times from +0.4 to +1.2 V vs reversible hydrogen electrode (RHE) showed an amorphous La oxide shell 1 – 2 nm thick. Bulk analyses showed that B-site leaching also occurs for samples soaked in 1 M KOH or pure EtOH. The mechanistic insights provided here should help inform the future design of La-based perovskite oxide electrocatalysts for alkaline fuel cells and stress the importance of stability metrics validating claims of promising electrocatalytic activity.