Effects of post-annealing on electrical properties of amorphous Ga-doped Zn–Sn–O semiconductor films

Abstract We investigated the effect of post-annealing on the electrical properties of amorphous gallium-zinc-tin oxide ( a -GZTO) films with different Ga contents. The films were deposited at room temperature by sputtering and annealed in air for 1 h. It was found that the doping with Ga, which acts as the carrier suppressor, contributes to the thermal stability of characteristic properties of a -GZTO thin films. The film with a small amount of Ga showed significant variations in carrier concentration according to the annealing temperature. Increases in carrier concentration and mobility can be ascribed to the reduction of subgap density of states by annealing. After annealing at 400 °C, however, the enrichment of Zn cations in surface region resulted in considerable changes in chemical bonding states and consequently, the carrier concentration decreased by two orders of magnitude for the low Ga-doped ZTO film.