Microstructures of high-growth-rate (up to 8.3 nm/s) microcrystalline silicon photovoltaic layers and their influence on the photovoltaic performance of thin-film solar cells

Abstract Microstructures of microcrystalline silicon (μc-Si) deposited at a high-growth-rate have been investigated in order to apply to the photovoltaic i-layer. μc-Si films were prepared by very-high-frequency (100 MHz) plasma-enhanced chemical vapor deposition at 180 °C. High growth rates of 3.3–8.3 nm/s have been achieved utilizing high deposition pressures up to 24 Torr and large input powers. Applying μc-Si to n–i–p junction solar cells, as the optimum result in this experimental series, a conversion efficiency of 6.30% (JSC: 22.1 mA/cm2, VOC: 0.470 V, and FF: 60.7%) has been achieved employing the i-layer deposited at 8.1 nm/s. Raman scattering and X-ray diffraction measurements revealed the crystalline volume fraction of around 50% with the (2 2 0) crystallographic preferential orientation, respectively. The cross-sectional transmission electron microscope image shows densely columnar structure grown directly on the underlying n-layer. These structural features are basically in good agreement those of low-growth-rate μc-Si used for a high efficiency solar cell as previously reported, implying advantages of the use of high pressures with regard to providing the photovoltaic i-layers. Finally, the implication is discussed from the photovoltaic performance as a function of the crystalline volume fraction of i-layer, and current problems in improving the photovoltaic performance are extracted.