Microwave-assisted hydrothermal synthesis of TiO2 spheres with efficient photovoltaic performance for dye-sensitized solar cells
Source abstract
Abstract
In this article, we present a microwave-assisted synthetic method to form micrometer size mesoporous TiO2 sphere for the application as photoanodes in dye-sensitized solar cells (DSCs). The material properties and photovoltaic performances are compared with commercial TiO2 paste and mesoporous sphere both fabricated by traditional hydrothermal method. The mesoporous TiO2 spheres were synthesized by controlled hydrolysis and subsequently grew with microwave heating. The microwave-synthesized mesoporous TiO2 spheres with diameters in the range from 400 to 600 nm are composed of 10 nm nanocrystals as building blocks and possess anatase crystal structure and high surface area (132.49 m2 g−1). The photovoltaic performances of DSCs using the photoanodes derived from hydrothermal mesoporous spheres and the microwave-synthesized mesoporous spheres yielded overall power conversion efficiencies of 5.89 and 5.43 % with the less volatile 3-methoxypropionitrile solvent electrolyte. The reaction time for crystallization process in the microwave heating was greatly shortened from 16 h to 80 min. The microwave-synthesized mesoporous spheres exhibit higher short-circuit photocurrent than commercial available hydrothermal nanocrystalline (JGC 18NRT). This is due to its superior scattering power in the entire visible and near-infrared regions, which enhanced the optical path in the photoactive medium. The incident photon to electron conversion efficiency results reflect that the better short-circuit current in the device made with microwave-synthesized mesoporous spheres electrodes is resulted from the increased light-harvesting efficiency in the red region. On the optimum condition with acetonitrile-based electrolyte, the microwave-synthesized mesoporous spheres electrode could deliver conversion efficiency of 6.19 % and higher value of 6.92 % by adding extra scattering layer of commercial paste (CCIC, HPW-400).
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: TiO2 Photocatalysis and Solar Cells · Advanced Photocatalysis Techniques · Quantum Dots Synthesis And Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (35)
Show source-provided references
1. Adachi M, Murata Y, Takao J, Jiu JT, Sakamoto M, Wang FM (2004) Highly efficient dye-sensitized solar cells with a titania thin-film electrode composed of a network structure of single-crystal-like TiO2 nanowires made by the “oriented attachment” mechanism. J Am Chem Soc 126(45):14943–1494910.1021/ja048068s ↗
2. Ayllón JA, Peiró AM, Saadoun L, Vigil E, Domènech X, Peral J (2000) Preparation of anatase powders from fluorine-complexed titanium(iv) aqueous solution using microwave irradiation. J Mater Chem 10(8):1911–191410.1039/b002723p ↗
3. Chen D, Huang F, Cheng Y-B, Caruso RA (2009) Mesoporous anatase TiO2 beads with high surface areas and controllable pore sizes: a superior candidate for high-performance dye-sensitized solar cells. Adv Mater 21(21):2206–221010.1002/adma.200802603 ↗
4. Chen D, Cao L, Huang F, Imperia P, Cheng Y-B, Caruso RA (2010) Synthesis of monodisperse mesoporous titania beads with controllable diameter, high surface areas, and variable pore diameters (14–23 nm). J Am Chem Soc 132(12):4438–444410.1021/ja100040p ↗
5. Furusawa T, Honda K, Ukaji E, Sato M, Suzuki N (2008) The microwave effect on the properties of silica-coated TiO2 fine particles prepared using sol–gel method. Mater Res Bull 43(4):946–95710.1016/j.materresbull.2007.04.031 ↗
6. Hart JN, Cervini R, Cheng YB, Simon GP, Spiccia L (2004) Formation of anatase TiO2 by microwave processing. Sol Energy Mater Sol Cells 84(1–4):135–14310.1016/j.solmat.2004.02.041 ↗
7. He Z, Zhu Z, Li J, Zhou J, Wei N (2011) Characterization and activity of mesoporous titanium dioxide beads with high surface areas and controllable pore sizes. J Hazard Mater 190(1–3):133–13910.1016/j.jhazmat.2011.03.011 ↗
8. Hore S, Vetter C, Kern R, Smit H, Hinsch A (2006) Influence of scattering layers on efficiency of dye-sensitized solar cells. Sol Energy Mater Sol Cells 90(9):1176–118810.1016/j.solmat.2005.07.002 ↗
9. Huang F, Chen D, Zhang XL, Caruso RA, Cheng Y-B (2010) Dual-function scattering layer of submicrometer-sized mesoporous TiO2 beads for high-efficiency dye-sensitized solar cells. Adv Funct Mater 20(8):1301–130510.1002/adfm.200902218 ↗
10. Huang C-H, Yang Y-T, Doong R-A (2011) Microwave-assisted hydrothermal synthesis of mesoporous anatase TiO2 via sol–gel process for dye-sensitized solar cells. Microporous Mesoporous Mater 142(2–3):473–48010.1016/j.micromeso.2010.12.038 ↗
11. Ito S, Chen P, Comte P, Nazeeruddin MK, Liska P, Péchy P, Grätzel M (2007) Fabrication of screen-printing pastes from TiO2 powders for dye-sensitised solar cells. Prog Photovoltaics Res Appl 15(7):603–61210.1002/pip.768 ↗
12. Jung H-G, Kang YS, Sun Y-K (2010) Anatase TiO2 spheres with high surface area and mesoporous structure via a hydrothermal process for dye-sensitized solar cells. Electrochim Acta 55(15):4637–464110.1016/j.electacta.2010.03.031 ↗
13. Kelly KL, Coronado E, Zhao LL, Schatz GC (2002) The optical properties of metal nanoparticles: the influence of size, shape, and dielectric environment. J Phys Chem B 107(3):668–67710.1021/jp026731y ↗
14. Kim YJ, Lee MH, Kim HJ, Lim G, Choi YS, Park N-G, Kim K, Lee WI (2009) Formation of highly efficient dye-sensitized solar cells by hierarchical pore generation with nanoporous TiO2 spheres. Adv Mater 21(36):3668–367310.1002/adma.200900294 ↗
15. Koide N, Islam A, Chiba Y, Han L (2006) Improvement of efficiency of dye-sensitized solar cells based on analysis of equivalent circuit. J Photochem Photobiol A 182(3):296–30510.1016/j.jphotochem.2006.04.030 ↗
16. Komarneni S, Katsuki H (2010) Microwave–hydrothermal synthesis of barium titanate under stirring condition. Ceram Int 36(3):1165–116910.1016/j.ceramint.2009.12.016 ↗
17. Komarneni S, Rajha RK, Katsuki H (1999) Microwave–hydrothermal processing of titanium dioxide. Mater Chem Phys 61(1):50–5410.1016/S0254-0584(99)00113-3 ↗
18. Li Y, Li H, Li T, Li G, Cao R (2009) Facile synthesis of mesoporous titanium dioxide nanocomposites with controllable phase compositions by microwave-assisted esterification. Microporous Mesoporous Mater 117(1–2):444–44910.1016/j.micromeso.2008.06.042 ↗
19. Liuxue Z, Xiulian W, Peng L, Zhixing S (2007) Photocatalytic activity of anatase thin films coated cotton fibers prepared via a microwave assisted liquid phase deposition process. Surf Coat Technol 201(18):7607–761410.1016/j.surfcoat.2007.02.004 ↗
20. Luo HL, Sheng J, Wan YZ (2008) Preparation and characterization of TiO2/polystyrene core–shell nanospheres via microwave-assisted emulsion polymerization. Mater Lett 62(1):37–4010.1016/j.matlet.2007.04.108 ↗
21. O’Regan B, Grätzel M (1991) A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO2 films. Nature 353(6346):737–74010.1038/353737a0 ↗
22. Parmar KPS, Ramasamy E, Lee J, Lee JS (2011) Rapid ([similar]10 min) synthesis of single-crystalline, nanorice TiO2 mesoparticles with a high photovoltaic efficiency of above 8%. Chem Commun 47(30):8572–857410.1039/c1cc12150b ↗
23. Periyat P, Leyland N, McCormack DE, Colreavy J, Corr D, Pillai SC (2010) Rapid microwave synthesis of mesoporous TiO2 for electrochromic displays. J Mater Chem 20(18):3650–365510.1039/b924341k ↗
24. Ribbens S, Meynen V, Tendeloo GV, Ke X, Mertens M, Maes BUW, Cool P, Vansant EF (2008) Development of photocatalytic efficient Ti-based nanotubes and nanoribbons by conventional and microwave assisted synthesis strategies. Microporous Mesoporous Mater 114(1–3):401–40910.1016/j.micromeso.2008.01.028 ↗
25. Rothenberger G, Comte P, Gratzel M (1999) A contribution to the optical design of dye-sensitized nanocrystalline solar cells. Sol Energy Mater Sol Cells 58(3):321–33610.1016/S0927-0248(99)00015-X ↗
26. Sauvage F, Chen D, Comte P, Huang F, Heiniger L-P, Cheng Y-B, Caruso RA, Grätzel M (2010) Dye-sensitized solar cells employing a single film of mesoporous TiO2 beads achieve power conversion efficiencies over 10%. ACS Nano 4(8):4420–442510.1021/nn1010396 ↗
27. Wang H-E, Zheng L-X, Liu C-P, Liu Y-K, Luan C-Y, Cheng H, Li YY, Martinu L, Zapien JA, Bello I (2011) Rapid microwave synthesis of porous TiO2 spheres and their applications in dye-sensitized solar cells. J Phys Chem C 115(21):10419–1042510.1021/jp2011588 ↗
28. Wilson GJ, Matijasevich AS, Mitchell DRG, Schulz JC, Will GD (2006) Modification of TiO2 for enhanced surface properties: finite Ostwald ripening by a microwave hydrothermal process. Langmuir 22(5):2016–202710.1021/la052716j ↗
29. Yan K, Qiu Y, Chen W, Zhang M, Yang S (2011) A double layered photoanode made of highly crystalline TiO2 nanooctahedra and agglutinated mesoporous TiO2 microspheres for high efficiency dye sensitized solar cells. Energy Environ Sci 4(6):2168–217610.1039/c1ee01071a ↗
30. Yang W-G, Wan F-R, Chen Q-W, Li J-J, Xu D-S (2010) Controlling synthesis of well-crystallized mesoporous TiO2 microspheres with ultrahigh surface area for high-performance dye-sensitized solar cells. J Mater Chem 20(14):2870–287610.1039/b923105f ↗
31. Yao BD, Zhang Y, Shi HZ, Zhang LD (2000) Fractal analysis of porous polycrystalline titania by adsorption. Chem Mater 12(12):3740–374410.1021/cm990674c ↗
32. Zhang Q, Cao G (2011) Hierarchically structured photoelectrodes for dye-sensitized solar cells. J Mater Chem 21(19):6769–677410.1039/c0jm04345a ↗
33. Zhang P, Yin S, Sato T (2009) Synthesis of high-activity TiO2 photocatalyst via environmentally friendly and novel microwave assisted hydrothermal process. Appl Catal B 89(1–2):118–12210.1016/j.apcatb.2008.12.002 ↗
34. Zumeta I, Ayllón JA, González B, Domenech X, Vigil E (2009) TiO2 films obtained by microwave-activated chemical-bath deposition used to improve TiO2-conducting glass contact. Sol Energy Mater Sol Cells 93(10):1728–173210.1016/j.solmat.2009.05.022 ↗
35. Zuo M-W, Li W, Shi J-L, Zeng Q (2006) Influence of CuO addition to BaSm2Ti4O12 microwave ceramics on sintering behavior and dielectric properties. Mater Res Bull 41(6):1127–113210.1016/j.materresbull.2005.11.005 ↗