Nearly 90% Circularly Polarized Emission in Monolayer WS2 Single Crystals by Chemical Vapor Deposition
Source abstract
Abstract
Monolayer transition-metal dichalcogenides (TMDCs) in the 2H-phase are promising semiconductors for opto-valleytronic and opto-spintronic applications because of their strong spin-valley coupling. Here, we report detailed studies of opto-valleytronic properties of heterogeneous domains in CVD-grown monolayer WS2 single crystals. By illuminating WS2 with off-resonance circularly polarized light and measuring the resulting spatially resolved circularly polarized emission (Pcirc), we find significantly large circular polarization (Pcirc up to 60% and 45% for α- and β-domains, respectively) already at 300 K, which increases to nearly 90% in the α-domains at 80 K. Studies of spatially resolved photoluminescence (PL) spectroscopy, Raman spectroscopy, X-ray photoelectron spectroscopy, Kelvin-probe force microscopy, and conductive atomic force microscopy reveal direct correlation among the PL intensity, defect densities, and chemical potential, with the α-domains showing lower defect densities and a smaller work function by 0.13 eV than the β-domains. This work function difference indicates the occurrence of type-two band alignments between the α- and β-domains. We adapt a classical model to explain how electronically active defects may serve as nonradiative recombination centers and find good agreement between experiments and the model. Scanning tunneling microscopic/spectroscopic (STM/STS) studies provide further evidence for tungsten vacancies (WVs) being the primary defects responsible for the suppressed PL and circular polarization in WS2. These results therefore suggest a pathway to control the opto-valleytronic properties of TMDCs by means of defect engineering.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: 2D Materials and Applications · Graphene research and applications · MXene and MAX Phase Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Applied Physics, California Institute of Technology, Pasadena, California 91125, United States
Department of Physics, California Institute of Technology, Pasadena, California 91125, United States
Division of Geological and Planetary Sciences, California Institute of Technology, Pasadena, California 91125, United States
Kavli Nanoscience Institute, California Institute of Technology, Pasadena, California 91125, United States
Funding
Army Research Office · Kavli Foundation · National Science Foundation
References (56)
Show source-provided references
1. 10.1073/pnas.050284810210.1073/pnas.0502848102 ↗
2. 10.1126/science.aac943910.1126/science.aac9439 ↗
3. 10.1039/C0NR00323A10.1039/C0NR00323A ↗
4. 10.1039/C8CS00255J10.1039/C8CS00255J ↗
5. 10.1038/nmat184910.1038/nmat1849 ↗
6. 10.1103/RevModPhys.83.83710.1103/RevModPhys.83.837 ↗
7. 10.1088/0957-4484/26/39/39560110.1088/0957-4484/26/39/395601 ↗
8. 10.1038/ncomms762010.1038/ncomms7620 ↗
9. 10.1021/nn406170d10.1021/nn406170d ↗
10. 10.1038/ncomms783510.1038/ncomms7835 ↗
11. 10.1038/nnano.2010.17210.1038/nnano.2010.172 ↗
12. 10.1038/nmat271110.1038/nmat2711 ↗
13. 10.1021/nl203249a10.1021/nl203249a ↗
14. 10.1021/acs.chemmater.7b0018310.1021/acs.chemmater.7b00183 ↗
15. 10.1021/nl301702r10.1021/nl301702r ↗
16. 10.1021/nl302015v10.1021/nl302015v ↗
17. 10.1038/nnano.2012.9510.1038/nnano.2012.95 ↗
18. 10.1038/nnano.2013.15110.1038/nnano.2013.151 ↗
19. 10.1021/nn506594a10.1021/nn506594a ↗
20. 10.1021/nn503988x10.1021/nn503988x ↗
21. 10.1021/acsnano.5b0696010.1021/acsnano.5b06960 ↗
22. 10.1038/nmat446510.1038/nmat4465 ↗
23. 10.1002/adma.20160504310.1002/adma.201605043 ↗
24. 10.1002/adfm.20170421010.1002/adfm.201704210 ↗
25. 10.1021/acsnano.7b0428710.1021/acsnano.7b04287 ↗
26. 10.1021/acsami.6b1628710.1021/acsami.6b16287 ↗
27. 10.1039/C7NR08303C10.1039/C7NR08303C ↗
28. 10.1088/2053-1583/2/2/02200110.1088/2053-1583/2/2/022001 ↗
29. 10.1021/acsnano.6b0491410.1021/acsnano.6b04914 ↗
30. 10.1038/nnano.2012.9610.1038/nnano.2012.96 ↗
31. 10.1063/1.476829910.1063/1.4768299 ↗
32. 10.1038/ncomms188210.1038/ncomms1882 ↗
33. 10.1103/PhysRevB.89.20530310.1103/PhysRevB.89.205303 ↗
34. 10.1103/PhysRevB.90.16130210.1103/PhysRevB.90.161302 ↗
35. 10.1103/PhysRevB.90.04141410.1103/PhysRevB.90.041414 ↗
36. 10.1038/srep2504110.1038/srep25041 ↗
37. 10.1021/nn400203810.1021/nn4002038 ↗
38. 10.1103/PhysRevB.86.08130110.1103/PhysRevB.86.081301 ↗
39. 10.1103/PhysRevLett.112.04740110.1103/PhysRevLett.112.047401 ↗
40. 10.1038/srep1888510.1038/srep18885 ↗
41. 10.1073/pnas.140696011110.1073/pnas.1406960111 ↗
42. 10.1021/acsnano.7b0856610.1021/acsnano.7b08566 ↗
43. 10.1557/jmr.2016.4710.1557/jmr.2016.47 ↗
44. 10.1002/adfm.20160041810.1002/adfm.201600418 ↗
45. 10.1021/nn505736z10.1021/nn505736z ↗
46. 10.1021/nl503636c10.1021/nl503636c ↗
47. 10.1038/srep0557510.1038/srep05575 ↗
48. 10.1038/srep0265710.1038/srep02657 ↗
49. 10.1039/C5NR00383K10.1039/C5NR00383K ↗
50. 10.1002/adfm.20160450910.1002/adfm.201604509 ↗
51. 10.1021/acsnano.7b0255410.1021/acsnano.7b02554 ↗
52. 10.1021/acs.nanolett.7b0130410.1021/acs.nanolett.7b01304 ↗
53. 10.1039/C5NR00188A10.1039/C5NR00188A ↗
54. 10.1021/acs.nanolett.7b0177010.1021/acs.nanolett.7b01770 ↗
55. 10.1016/j.ssc.2014.11.00510.1016/j.ssc.2014.11.005 ↗
56. 10.1039/C4RA06378C10.1039/C4RA06378C ↗