Brittle-to-Ductile Transition Temperature Decreases at the Microscale in Muscovite Mica

High Resolution Image Download MS PowerPoint Slide Characterizing the structural and chemical transitions of muscovite mica across various scales and thermal profiles is essential for ensuring the reliability of high-voltage power insulation, aerospace thermal barriers, and nanoscale semiconductor substrates under extreme operational stress. Here, we investigate notch fracture toughness K Ic n of muscovite mica as a function of feature size w and temperature T with microscale shear testing. K Ic n decreased and then stayed constant as w increased, likely from fabrication-induced changes to the microstructure and roughness. Moreover, K Ic n initially decreased and then increased as temperature T increased, with the reversal in trend indicative of a brittle-to-ductile transition. Complementary Raman spectroscopy and molecular dynamics showed that the observed trends were due to an increase in bond lengths and a decrease in critical stresses/strains. In comparing the microscale results to macroscale counterparts, it was surmised that the decrease in brittle-to-ductile transition temperature was due to an increase in the dehydroxylation rate.