Iodine’s Wild Ride Leading to Photoinstability in Halide Perovskite Solar Cells

High Resolution Image Download MS PowerPoint Slide Understanding processes that contribute to efficiency losses during long-term operation of perovskite solar cells is crucial for achieving operational stability. Although maximum power point tracking optimizes outdoor performance, it is not uncommon that devices are kept under open-circuit conditions during sunny hours. Under these conditions, charge carriers accumulate at the interfaces rather than flowing through the circuit. In the case of the MAPbI 3 /spiro-OMeTAD interface studied here, hole accumulation leads to formation of I 2 and subsequent oxidation of spiro-OMeTAD. By employing in situ absorption measurements, we show that the decrease in power conversion efficiency follows the spiro-OMeTAD oxidation while operating the device under open-circuit conditions. In short-circuit conditions, where photogenerated charge carriers are extracted in the external circuit, the I 2 -induced oxidation of spiro-OMeTAD and the device instability are minimized. The photoinduced expulsion of iodine from MAPbI 3 into spiro-OMeTAD discussed in this study provides new insight into the photoinstability of perovskite solar cells.