Bearing strength of pin‐connected polymer composites subjected to dynamic loading

Abstract In this study, static load bearing strength of pin‐connected carbon fiber‐reinforced polyphenylenesulphide (PPS) composites that have [(0°/90°)]_3s stacking sequence was investigated. Firstly, the samples were loaded dynamically, and then the same samples were loaded statically. The results obtained from this sequential experiment were compared with the results obtained from samples that were loaded only statically. In addition, the fatigue life and failure mechanisms were investigated with respect to the selection of the geometrical parameters. Dynamic and static loading experiments were performed according to the ASTM STP 749 and ASTM D953 standards, respectively. To obtain optimum load bearing values, the ratio of distance between the edge and hole center to hole diameter (E/D) and ratio of sample width to hole diameter (W/D) has been systematically changed. According to the experimental results, maximum load bearing values have been obtained when E/D ratio was equal to 2. POLYM. COMPOS., 2010. © 2009 Society of Plastics Engineers