Ethylene‐vinyl acetate copolymer/multiwalled carbon nanotube/organoclay nanocomposites
Source abstract
Abstract
Abstract Ethylene‐vinyl acetate copolymer (EVA) was melt‐mixed with multiwalled carbon nanotubes (MWCNTs) and organoclays, and the effects of simultaneous use of organoclays and MWCNTs on the surface resistivity and tensile properties of EVA nanocomposites were investigated. The surface resistivity of EVA/MWCNT nanocomposite with 1 phr of MWCNT is out of our measurement range (above 1012 Ω/square). With increasing content of organoclay from 0 to 3 phr, the surface resistivity of the EVA/MWCNT/organoclay nanocomposites with 1 phr MWCNT remains out of our measurement range. However, the surface resistivity of the nanocomposite decreases to 106 Ω/square with addition of 5 phr organoclay. The tensile properties of EVA/MWCNT/organoclay nanocomposites with 1 phr MWCNT and 5 phr organocaly are similar to those of EVA/MWCNT nanocomposites with 5 phr MWCNT except tensile modulus. POLYM. COMPOS. 2012. © 2012 Society of Plastics Engineers
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Polymer Nanocomposites and Properties · Conducting polymers and applications · Dielectric materials and actuators
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (40)
Show source-provided references
1. 10.1016/j.compscitech.2006.07.02710.1016/j.compscitech.2006.07.027 ↗
2. 10.1016/j.polymer.2005.06.09410.1016/j.polymer.2005.06.094 ↗
3. 10.1016/j.cplett.2006.10.08810.1016/j.cplett.2006.10.088 ↗
4. 10.1016/S0032-3861(03)00451-810.1016/S0032-3861(03)00451-8 ↗
5. 10.1016/j.polymer.2004.10.04010.1016/j.polymer.2004.10.040 ↗
6. 10.1016/S0032-3861(02)00151-910.1016/S0032-3861(02)00151-9 ↗
7. 10.1002/1439-2054(20020601)287:6<395::AID-MAME395>3.0.CO;2-S10.1002/1439-2054(20020601)287:6<395::AID-MAME395>3.0.CO;2-S ↗
8. 10.1021/cm051881h10.1021/cm051881h ↗
9. 10.1002/adma.20050185110.1002/adma.200501851 ↗
10. 10.1016/j.eurpolymj.2006.12.01510.1016/j.eurpolymj.2006.12.015 ↗
11. 10.1021/ma035594f10.1021/ma035594f ↗
12. 10.1021/ma049132t10.1021/ma049132t ↗
13. 10.1016/j.polymer.2005.12.02610.1016/j.polymer.2005.12.026 ↗
14. 10.1016/S0032-3861(03)00073-910.1016/S0032-3861(03)00073-9 ↗
15. 10.1016/j.polymer.2006.12.03510.1016/j.polymer.2006.12.035 ↗
16. 10.1016/j.polymer.2006.04.05110.1016/j.polymer.2006.04.051 ↗
17. 10.1016/j.polymer.2004.01.02310.1016/j.polymer.2004.01.023 ↗
18. 10.1002/polb.2111510.1002/polb.21115 ↗
19. 10.1002/app.1146910.1002/app.11469 ↗
20. 10.1016/j.carbon.2003.12.04310.1016/j.carbon.2003.12.043 ↗
21. 10.1002/pc.2005810.1002/pc.20058 ↗
22. 10.1163/15685540377195365010.1163/156855403771953650 ↗
23. 10.1016/S0009-2614(01)00186-510.1016/S0009-2614(01)00186-5 ↗
24. 10.1016/S0025-5408(01)00775-910.1016/S0025-5408(01)00775-9 ↗
25. 10.1002/1097-4628(20010103)79:1<125::AID-APP150>3.0.CO;2-D10.1002/1097-4628(20010103)79:1<125::AID-APP150>3.0.CO;2-D ↗
26. 10.1002/app.120010.1002/app.1200 ↗
27. 10.1007/s10853-005-1601-z10.1007/s10853-005-1601-z ↗
28. 10.1016/S0009-2614(00)01013-710.1016/S0009-2614(00)01013-7 ↗
29. 10.1016/S0927-796X(00)00012-710.1016/S0927-796X(00)00012-7 ↗
30. 10.1016/S0169-1317(99)00017-410.1016/S0169-1317(99)00017-4 ↗
31. 10.1002/adma.1996008010410.1002/adma.19960080104 ↗
32. 10.1016/j.progpolymsci.2003.08.00210.1016/j.progpolymsci.2003.08.002 ↗
33. 10.1002/pat.69110.1002/pat.691 ↗
34. 10.1166/jnn.2010.148510.1166/jnn.2010.1485 ↗
35. 10.1021/ma052256110.1021/ma0522561 ↗
36. 10.1016/j.tca.2005.02.03110.1016/j.tca.2005.02.031 ↗
37. 10.1016/j.polymdegradstab.2005.03.02310.1016/j.polymdegradstab.2005.03.023 ↗
38. 10.1002/app.1192210.1002/app.11922 ↗
39. 10.1016/S0141-3910(02)00065-410.1016/S0141-3910(02)00065-4 ↗
40. 10.1002/mame.20040010910.1002/mame.200400109 ↗