Mechanical performance of woven carbon fabric reinforced pCBT composites with nanosilica particles
Source abstract
Abstract
The effect of nanosilica content (0, 0.5, and 2 wt%) on mechanical performance of carbon fabric woven cloth reinforced polymerized poly(butylene terephthalate) resin composites (CF/pCBT) is investigated. The catalyst and nanosilica particles are added on the prepreg surface, and hot‐press processing is adopted in order to manufacture CF/pCBT composites. The experimental results reveal that nanosilica could enhance the mechanical performance of CF/pCBT composites. After adding nanosilica in the composites, elastic modulus enhances 23.96%, and Mode‐II fracture toughness increases 380.43%. Scanning electron microscope observation shows that dispersity of nanoparticles in composites plays an important role on the overall mechanical performance of the obtained composites. Furthermore, failure mechanism has been analyzed according to the damage morphology. POLYM. COMPOS., 38:2528–2535, 2017. © 2015 Society of Plastics Engineers
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Epoxy Resin Curing Processes · Fiber-reinforced polymer composites · Polymer Nanocomposites and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Smart Structures and Advanced Composites Laboratory, College of Aerospace and Civil Engineering, Harbin Engineering University Harbin 150001 China
Funding
National Natural Science Foundation of China
References (41)
Show source-provided references
1. 10.1016/j.progpolymsci.2006.08.00810.1016/j.progpolymsci.2006.08.008 ↗
2. 10.1007/s10973-005-7059-z10.1007/s10973-005-7059-z ↗
3. 10.1021/ma02136410.1021/ma021364 ↗
4. 10.1021/ma048387410.1021/ma0483874 ↗
5. 10.1002/pen.2205010.1002/pen.22050 ↗
6. 10.1016/j.tca.2009.04.00410.1016/j.tca.2009.04.004 ↗
7. 10.1002/pen.2191010.1002/pen.21910 ↗
8. 10.1016/j.compositesa.2008.08.00410.1016/j.compositesa.2008.08.004 ↗
9. 10.1016/j.polymer.2005.07.08210.1016/j.polymer.2005.07.082 ↗
10. 10.1016/j.compscitech.2006.09.01210.1016/j.compscitech.2006.09.012 ↗
11. 10.1016/j.compositesa.2008.12.00310.1016/j.compositesa.2008.12.003 ↗
12. 10.1023/A:100468670863910.1023/A:1004686708639 ↗
13. 10.1016/j.compositesa.2009.08.01410.1016/j.compositesa.2009.08.014 ↗
14. 10.1016/j.actamat.2008.01.00210.1016/j.actamat.2008.01.002 ↗
15. 10.1016/j.compositesb.2008.01.00210.1016/j.compositesb.2008.01.002 ↗
16. 10.1007/s10853-006-1420-x10.1007/s10853-006-1420-x ↗
17. 10.1016/j.polymer.2006.11.03810.1016/j.polymer.2006.11.038 ↗
18. 10.1016/j.compscitech.2011.12.01510.1016/j.compscitech.2011.12.015 ↗
19. 10.1016/j.polymer.2008.09.02710.1016/j.polymer.2008.09.027 ↗
20. Zhang H. · Acta Mater. · 2006 · 54 · 183
21. 10.1016/j.compscitech.2008.01.00910.1016/j.compscitech.2008.01.009 ↗
22. 10.1080/03602559.2010.49643010.1080/03602559.2010.496430 ↗
23. 10.1039/b603020c10.1039/b603020c ↗
24. Zhang C.Q. · J. Appl. Polym. Sci. · 2015 · 132
25. 10.1016/j.polymer.2015.05.04610.1016/j.polymer.2015.05.046 ↗
26. 10.1166/jnn.2010.279110.1166/jnn.2010.2791 ↗
27. 10.1016/j.compositesa.2004.11.01710.1016/j.compositesa.2004.11.017 ↗
28. 10.1177/002199830934531710.1177/0021998309345317 ↗
29. 10.1016/j.compscitech.2008.02.02610.1016/j.compscitech.2008.02.026 ↗
30. 10.1177/002199830934613810.1177/0021998309346138 ↗
31. 10.1016/j.compositesa.2005.12.02710.1016/j.compositesa.2005.12.027 ↗
32. 10.1016/j.carbon.2009.06.03910.1016/j.carbon.2009.06.039 ↗
33. 10.1016/j.carbon.2011.06.04710.1016/j.carbon.2011.06.047 ↗
34. 10.1016/j.carbon.2012.09.01110.1016/j.carbon.2012.09.011 ↗
35. 10.1016/j.compstruct.2012.12.01810.1016/j.compstruct.2012.12.018 ↗
36. 10.1177/002199831038908810.1177/0021998310389088 ↗
37. 10.1088/1468-6996/15/3/03500410.1088/1468-6996/15/3/035004 ↗
38. 10.1016/j.compscitech.2013.06.00110.1016/j.compscitech.2013.06.001 ↗
39. 10.1016/j.compscitech.2009.06.02010.1016/j.compscitech.2009.06.020 ↗
40. 10.1002/app.1966.07010010710.1002/app.1966.070100107 ↗
41. 10.1002/app.3974910.1002/app.39749 ↗