Forced torsional properties of PMR composites with varying nadic ester concentrations and processing histories

Abstract PMR polyimide resin was prepared from 4,4′‐methylenedianiline (MDA), the dimethyl ester of 3,3′,4,4′‐ benzophenonetetracarboxylic acid (BTDE) and the monomethyl ester of 5‐norbornene‐2,3‐dicarboxylic acid (NE). The NE group serves as a chain terminator and crosslinking site. PMR/Celion 6000 composites were fabricated from resins having varying NE concentrations using two molding processes, and the laminates characterized in forced torsion. Glass transition temperatures (T_g) of 360–390°C were observed in the crosslinked resins, as compared with the literature value of 284°C reported for the uncrosslinked systemT_g did not decrease with decreasing NE concentrations over the range from 2.0 to 1.25 moles. Stoichiometry, within the range studied, showed little influence on shear properties; however, a 25% variation in matrix shear modulus with processing was observed. The G₁₂ values determined in forced torsion were in excellent agreement with those reported from tensile tests of ±45° laminates. A branching and possible secondary crosslink mechanism is proposed based on dynamic mechanical behavior and infrared spectra of the composites.