In situ composites based on blends of a polyetherimide and thermotropic liquid crystalline polymers subjected to shearfree deformations

Abstract The effects of shearfree elongational flows on the morphology and mechanical properties of blends of a polyetherimide (PEI) with thermotropic liquid crystalline polymers (TLCP) have been investigated. Extruded sheets and injection molded plaques of PEI/Vectra A and PEI/HX1000 blends, with a TLCP concentration of ≤30 wt%, were subjected to uniaxial elongation, planar and biaxial deformations at 240°C, above the glass transition temperature of the PEI, and at 265°C, which is below the melting point of the TLCPs. Experimental results revealed that each particular mode of shearfree deformation had a distinct effect on the morphology and properties of the blends. For instance, TLCP droplets were deformed into elongated fibrils by application of uniaxial elongation, deformed into elongated ribbon‐like structures after planar deformation, and deformed into a disc‐like shape by application of equibiaxial flow. Regarding mechanical properties, it was observed that the tensile modulus and strength of molded plaques of PEI/HX1000 80/20 wt% increased to about twice their initial values (from 5.13 to 10.40 GPa and from 105 to 198 MPa, respectively) after a strain of 0.75 was applied in a direction parallel to the initial direction of the TLCP fibers. In addition, samples exhibiting equal values of flow and transverse direction tensile modulus of ∼5.0 GPa were obtained when molded plaques of PEI/HX1000 80/20 wt% were subjected to planar stretching in a direction transverse to the initial direction of the fibers. Thus, by subjecting injection molded plaques to planar stretching, it was possible to obtain a sample exhibiting balanced flow and transverse direction mechanical properties and, consequently, reduced anisotropy.